Carbonation

แปลว่า(Concrete Engineering) 1) Reaction between the products of portland cement (soluble calcium hydroxides), water and carbon dioxide to produce insoluble calcium carbonate (efflorescence). 2) Soft white, chalky surface dusting of freshly placed, unhardened concrete caused by carbon dioxide from unvented heaters or gasoline powered equipment in an enclosed space. 3) Carbonated, dense, impermeable to absorption, top layer of the surface of concrete caused by surface reaction to carbon dioxide. This carbonated layer becomes denser and deeper over a period of time. 4) Reaction with carbon dioxide which produces a slight shrinkage in concrete. Improves chemical stability. Concrete masonry units during manufacturing may be deliberately exposed to carbon dioxide after reaching 80% strength to induce carbonation shrinkage to make the units more dimensionally stable. Future drying shrinkage is reduced by as much as 30%.

hip rafter

แปลว่าตะเข้สัน

A Coatings

แปลว่า(English) Coatings on hot-dipped galvanized steels processed to convert the coating completely to zinc-iron alloys; dull gray in appearance, have no spangle, and after proper preparation, are well suited for painting.

Pumping (of Pavements)

แปลว่า(Concrete Engineering) The ejection of a mixture of water and solid materials such as clay or silt along cracks, transverse or longitudinal joints, and along pavement edges caused by downward slab movement due to the passage of heavy loads, machinery or equipment over the pavement after free water has accumulated in or on the subbase, subgrade or basecourse.

Neat Cement-Paste

แปลว่า(Concrete Engineering) A mixture of water and hydraulic cement, both before and after setting and hardening.

Debugging

แปลว่า(Software Engineering) the activity associated with finding and correcting an error or defect - a lack of conformance to requirements found in the software after delivery to the customer

Secondary treatment

แปลว่า(Environmental Engineering) In wastewater treatment, the conversion of the suspended, colloidal and dissolved organics remaining after primary treatment into a microbial mass with is then removed in a second sedimentation process. Secondary treatment included both the biological process and the associated sedimentation process.

Blue Brittleness

แปลว่า(english) Brittleness exhibited by some steels after being heated to some temperature within the range of 300 (degrees) to 650 (degrees) F, and more especially if the steel is worked at the elevated temperature. Killed steels are virtually free of this kind of brittleness.

Age Hardening

แปลว่า(english) Hardening by aging, usually after rapid cooling or cold working. The term as applied to soft, or low carbon steels, relates to a wide variety of commercially important, slow, gradual changes that take place in properties of steels after the final treatment. These changes, which bring about a condition of increased hardness, elastic limit, and tensile strength with a consequent loss in ductility, occur during the period in which the steel is at normal temperatures.

After all

แปลว่าสุดท้ายแล้ว, นอกจากนั้น

Be After

กริยาช่อง 2Were After

กริยาช่อง 3Been After

แปลว่าหลังจากนั้น

Name After

กริยาช่อง 2Named After

กริยาช่อง 3Named After