Inelastic:

แปลว่า(english) Not surprisingly, the opposite of elastic. A deformation of a structure or material under load is described as inelastic when the deformation remains after the load is removed. The term plastic is often used with the same meaning.

Aging 2

แปลว่า(english) A change in properties that occurs at ambient or moderately elevated temperatures after hot working or a heat treating operation (quench aging in ferrous alloys), or after a cold working operation (strain aging). The change in properties is often, but not always, due to a phase change (precipitation), but does not involve a change in chemical composition. In a metal or alloy, a change in properties that generally occurs slowly at room temperature and more rapidly at higher temperatures.

Secondary treatment

แปลว่า(Environmental Engineering) In wastewater treatment, the conversion of the suspended, colloidal and dissolved organics remaining after primary treatment into a microbial mass with is then removed in a second sedimentation process. Secondary treatment included both the biological process and the associated sedimentation process.

Blue Brittleness

แปลว่า(english) Brittleness exhibited by some steels after being heated to some temperature within the range of 300 (degrees) to 650 (degrees) F, and more especially if the steel is worked at the elevated temperature. Killed steels are virtually free of this kind of brittleness.

Toxicity

แปลว่า(Environmental Engineering) A U.S. EPA hazardous waste characteristic defined with a rigorous test procedure, the TCLP (for Toxicity Characteristic Leaching Procedure). In the procedure, a waste is extracted for 24 hours with an acetic acid solution. The acid extract is then analyzed for the presence of any of the contaminants listed in the procedure.

Aging 1

แปลว่า(english) A change in the properties of certain metal and alloys (such as steel) that occurs at ambient or moderately elevated temperatures after a hot working heat treatment or cold working operation. Typical properties impacted are hardness, yield strength, tensile strength, ductility, impact value, formability, magnetic properties, etc. See also Non-aging.

Pumping (of Pavements)

แปลว่า(Concrete Engineering) The ejection of a mixture of water and solid materials such as clay or silt along cracks, transverse or longitudinal joints, and along pavement edges caused by downward slab movement due to the passage of heavy loads, machinery or equipment over the pavement after free water has accumulated in or on the subbase, subgrade or basecourse.

Basic Oxygen Furnace (BOF)

แปลว่า(english) "WHAT A pear-shaped furnace, lined with refractory bricks, that refines molten iron from the blast furnace and scrap into steel. Up to 30% of the charge into the BOF can be scrap, with hot metal accounting for the rest. WHY BOFs, which can refine a heat (batch) of steel in less than 45 minutes, replaced open-hearth furnaces in the 1950s; the latter required five to six hours to process the metal. The BOF's rapid operation, lower cost and ease of control give it a distinct advantage over previous methods. HOW Scrap is dumped into the furnace vessel, followed by the hot metal from the blast furnace. A lance is lowered from above, through which blows a high-pressure stream of oxygen to cause chemical reactions that separate impurities as fumes or slag. Once refined, the liquid steel and slag are poured into separate containers. "

Carbonation

แปลว่า(Concrete Engineering) 1) Reaction between the products of portland cement (soluble calcium hydroxides), water and carbon dioxide to produce insoluble calcium carbonate (efflorescence). 2) Soft white, chalky surface dusting of freshly placed, unhardened concrete caused by carbon dioxide from unvented heaters or gasoline powered equipment in an enclosed space. 3) Carbonated, dense, impermeable to absorption, top layer of the surface of concrete caused by surface reaction to carbon dioxide. This carbonated layer becomes denser and deeper over a period of time. 4) Reaction with carbon dioxide which produces a slight shrinkage in concrete. Improves chemical stability. Concrete masonry units during manufacturing may be deliberately exposed to carbon dioxide after reaching 80% strength to induce carbonation shrinkage to make the units more dimensionally stable. Future drying shrinkage is reduced by as much as 30%.