ผลการค้นหา

Secured landfill

แปลว่า(Environmental Engineering) A landfill which has containment measures such as liners and a leachate collection system so that materials placed in the landfill will not migrate into the surrounding soil, air and water.

Bright Annealing

แปลว่า(english) A process carried out usually in a controlled furnace atmosphere, so surface does not oxidize, remaining bright.

Agglomerating Processes

แปลว่า(english) "Fine particles of limestone (flux) and iron ore are difficult to handle and transport because of dusting and decomposition, so the powdery material usually is processed into larger pieces. The raw material's properties determine the technique that is used by mills. 1) SINTER Baked particles that stick together in roughly one-inch chunks. Normally used for iron ore dust collected from the blast furnaces. 2) PELLETS Iron ore or limestone particles are rolled into little balls in a balling drum and hardened by heat. 3) BRIQUETTES Small lumps are formed by pressing material together. Hot Iron Briquetting (HBI) is a concentrated iron ore substitute for scrap for use in electric furnaces.

Bright Annealing 2

แปลว่า(english) The process of annealing in a protective atmosphere so as to prevent discoloration of the bright surface desired.

Bastard

แปลว่า(english) Threads,parts,tools and sizes that are not standard, such as, “Bastard Nuts”, “Bastard Plus”, “bastaard fittings and so forth. The term also refers to a standard coarse cut file.

Construction Joint

แปลว่า(Concrete Engineering) The contact between the placed concrete and concrete surfaces, against or upon which concrete is to be placed and to which new concrete is to adhere, that has become so rigid that the new concrete cannot be incorporated integrally by vibration with that previously placed. Unformed construction joints are horizontally placed or nearly so.

Bainite

แปลว่า(english) A eutectoid transformation product of ferrite and a fine dispersion of carbide, generally formed at temperatures below 840 to 930 F (450 to 500 C): upper bainite is an aggregate containing parallel lath-shape units of ferrite, produces the so-called feathery appearance in optical microscopy, and is formed at temperatures above about 660 F (350 C); lower bainite consists of individual plate-shape units and is formed at temperatures below about 660 F (350 C). Also, a slender, needle-like (acicular) microstructure appearing in spring steel strip characterized by toughness and greater ductility than tempered Martensite. Bainite is a decomposition product of Austenite best developed at interrupted holding temperatures below those forming fine pearlite and above those giving Martensite.

Black Plate

แปลว่า(english) A light weight or a thin uncoated steel sheet or strip so called because of its dark oxide coloring prior to pickling. It is manufactured by two different processes. (1) Form sheet bar on single stand sheet mills or sheet mills in tandem. This method is now almost obsolete. (2) On modern, high speed continuous tandem cold reduction mills from coiled hot rolled pickled wide strip into ribbon wound coils to finished gage. Sizes range from 12 to 32 in width, and in thicknesses from 55 lbs. to 275 lbs. base box weight. It is used either as is for stampings, or may be enameled or painted or tin or terne coated.

Bessemer Process

แปลว่า(english) A process for making steel by blowing air through molten pig iron contained in a refractory lined vessel so that the impurities are thus removed by oxidation.

Bright Annealed Wire

แปลว่า(english) Steel wire bright drawn and annealed in controlled non-oxidizing atmosphere so that surface oxidation is reduced to a minimum and the surface remains relatively bright.

Adiabatic Curing

แปลว่า(Concrete Engineering) The maintenance of ambient conditions during the setting and hardening of concrete so that heat is neither lost nor gained from the surroundings of the concrete.

Adapters

แปลว่า(english) Steel segments that are bolted to the reel mandrel to increase their diameter so that large (24" ID) coils can be run.