Cement Gel

แปลว่า(Concrete Engineering) The colloidal gel (glue like) material that makes up the major portion of the porous mass of which hydrated cement paste is composed.

AAC - Autoclaved Aerated Concrete

แปลว่า(Concrete Engineering) Exceptionally lightweight precast concrete with high thermal qualities and fire resistence. Suitable for cutting with ordinary hand tools. Mix design is composed of portland cement, sand or siliceous material, lime, gypsum, finely powdered aluminum, and water. Initial mix is a combination of portland cement, sand, lime and gypsum to produce a slurry. Finely powdered aluminum mixed into a paste is added prior to placement into large, rail-like forms. The finely powdered aluminum reacts with the alkaline components of the cement and lime to produce hydrogen gas, which increases the volume approximately five times producing a uniformly, dispersed cellular structure. Units are cut to required shape. Units are placed in an autoclave, an enclosed pressurized chamber, and steam cured at 3500 F. Approximately 80% of the ultimate volume consists of air voids.

Cementitious

แปลว่า(Concrete Engineering) Having cement-like, cementing, or bonding type properties. Material or substance producing bonding properties or cement-like materials.

chain like fencing

แปลว่ารั้วเหล็ก ขัดเป็นลูกโซ่ แบบตะแกรง

Greenhouse gases

แปลว่า(Environmental Engineering) Gases which trap solar radiation. Of the solar energy entering the earth's atmosphere a portion is reflected back and a portion penetrates onto the earth's surface. The portion reflected back from the earth's surface is at a different wavelength that when it entered. Carbon dioxide and other gases, which pass solar radiation, absorb this reflected radiation, increasing the earth's temperature. This is much like a greenhouse, hence the name.

PDL

แปลว่า(Software Engineering) program design language; a combination of natural language with programming language-like constructs

Ion exchange

แปลว่า(Environmental Engineering) An adsorption process in which one ion is exchanged for another ion of like charge. There is an equivalence of exchanged charge.

Buckles

แปลว่า(english) Appeaars like a series of waves and are created during rolling as a result of mechanical misalignment or cross-section irregularities in supply coil.

Bainite

แปลว่า(english) A eutectoid transformation product of ferrite and a fine dispersion of carbide, generally formed at temperatures below 840 to 930 F (450 to 500 C): upper bainite is an aggregate containing parallel lath-shape units of ferrite, produces the so-called feathery appearance in optical microscopy, and is formed at temperatures above about 660 F (350 C); lower bainite consists of individual plate-shape units and is formed at temperatures below about 660 F (350 C). Also, a slender, needle-like (acicular) microstructure appearing in spring steel strip characterized by toughness and greater ductility than tempered Martensite. Bainite is a decomposition product of Austenite best developed at interrupted holding temperatures below those forming fine pearlite and above those giving Martensite.

Capillarity

แปลว่า(Concrete Engineering) A wick-like action whereby a liquid will migrate vertically through material, in a upward direction; as oil in a lamp travels upward through the wick,

Break Test (for tempered steel)

แปลว่า(english) A method of testing hardened and tempered high carbon spring steel strip wherein the specimen is held and bent across the grain in a vice-like calibrated testing machine. Pressure is applied until the metal fractures at which point a reading is taken and compared with a standard chart of brake limitations for various thickness ranges.

Black Oil Tempered Spring Steel Strip (Scaleless Blue)

แปลว่า(english) A flat cold rolled usually .70/.80 medium high carbon steel strip, blue-black in color, which has been quenched in oil and drawn to desired hardness. While it looks and acts much like blue tempered spring steel and carries a Rockwell hardness of C44/47, it has not been polished and is lower in carbon content. Used for less exacting requirements than clock spring steel, such as snaps, lock springs, hold down springs, trap springs, etc. It will take a more severe bend before fracture than will clock spring, but it does not have the same degree of spring-back.