ผลการค้นหา

Calcareous

แปลว่า(Concrete Engineering) Containing calcium carbonate or, less generally, containing the element calcium.

Acetyl Tributyl Citrate

แปลว่า(english) One of the lubricating oils generally applied on tin Mill Products (tin plate, TFS-chrome/chrome oxide coated steel, and blackplate).

Bainite

แปลว่า(english) A eutectoid transformation product of ferrite and a fine dispersion of carbide, generally formed at temperatures below 840 to 930 F (450 to 500 C): upper bainite is an aggregate containing parallel lath-shape units of ferrite, produces the so-called feathery appearance in optical microscopy, and is formed at temperatures above about 660 F (350 C); lower bainite consists of individual plate-shape units and is formed at temperatures below about 660 F (350 C). Also, a slender, needle-like (acicular) microstructure appearing in spring steel strip characterized by toughness and greater ductility than tempered Martensite. Bainite is a decomposition product of Austenite best developed at interrupted holding temperatures below those forming fine pearlite and above those giving Martensite.

Aging 2

แปลว่า(english) A change in properties that occurs at ambient or moderately elevated temperatures after hot working or a heat treating operation (quench aging in ferrous alloys), or after a cold working operation (strain aging). The change in properties is often, but not always, due to a phase change (precipitation), but does not involve a change in chemical composition. In a metal or alloy, a change in properties that generally occurs slowly at room temperature and more rapidly at higher temperatures.

Burnt Rubber

แปลว่า(english) Small or large black spots that generally show up on surface and are generally caused by pickling steel too hot.

Ductility:

แปลว่า(english) Ductility generally refers to the amount of inelastic deformation which a material or structure experiences before complete failure. Quantitatively, ductility can be defined as the ratio of the total displacement or strain at failure, divided by the displacement or strain at the elastic limit.

Yield stress:

แปลว่า(english) A material loaded beyond its yield stress, no longer exhibits linear elastic behavior. Metals, particularly mild steel, generally have a very well defined yield stress compared to other materials. Yield stress is sometimes called yield strength.

Butcher Saw Steel

แปลว่า(english) A hardened, tempered, and polished high carbon spring steel strip material (carbon content is generally higher than that of a material used for wood band saw applications) with a Rockwell value of roughly C47/49.

Maximum Size Aggregate

แปลว่า(Concrete Engineering) Aggregate whose largest particle size is present in sufficient quantity to affect the physical properties of concrete; generally designated by the sieve size on which the maximum amount permitted to be retained is 5 or 10 percent by weight.

Brinell Hardness Testing

แปลว่า(english) Method of determining the hardness of materials; involves impressing a hardened ball of specified diameter into the material surface at a known pressure (10-mm ball, 500-kg load for aluminum alloys). The Brinell hardness number results from calculations involving the load and the spherical area of the ball impression. Direct-reading testing are generally used for routine inspection of forgings, and as a heat treat control function.

Vibration

แปลว่า(Concrete Engineering) Energetic agitation of concrete to assist in its consolidation, produced by mechanical oscillating devices at moderately high frequencies. (A.) External vibration employs a device attached to the forms and is particularly applicable to the manufacture of precast items and for the vibration of tunnel lining forms. (B.) Internal vibration employs an element which can be inserted into the concrete; and is more generally used for cast-in-place construction.

Brown Sharp Gages

แปลว่า(english) A standard series of sizes refered to by numbers, in which the diameter of wire or thickness of sheet metal is generally produced and which is used in the manufacture of brass, bronze, copper, copper-base alloys and aluminum. These gage numbers have a definite relationship to each other. In this system, the decimal thickness is reduced by 50% every six gage numbers- while temper is expressed by the number of B&S gage numbers as cold reduced in thickness from previous annealing. For each B&S gage number in thickness reduction, where is assigned a hardness value of 1/4 hard.