ผลการค้นหา

ค้นเจอ 42 รายการ

Bainite

(english) A eutectoid transformation product of ferrite and a fine dispersion of carbide, generally formed at temperatures below 840 to 930 F (450 to 500 C): upper bainite is an aggregate containing parallel lath-shape units of ferrite, produces the so-called feathery appearance in optical microscopy, and is formed at temperatures above about 660 F (350 C); lower bainite consists of individual plate-shape units and is formed at temperatures below about 660 F (350 C). Also, a slender, needle-like (acicular) microstructure appearing in spring steel strip characterized by toughness and greater ductility than tempered Martensite. Bainite is a decomposition product of Austenite best developed at interrupted holding temperatures below those forming fine pearlite and above those giving Martensite.

Organic nitrogen

(Environmental Engineering) Nitrogen contained as amines in organic compounds such as amino acids and proteins.

BREATHER

(english) A device which permits air to move in and out of a container or component to maintain atmospheric pressure.

Dry Rodded Weight

(Concrete Engineering) The weight of dry aggregate rodded into a cylindrical container of diameter approximately equal to the height, each of 3 layers rodded 25 times, and the excess aggregate struck off level with the top of the container

Basket Screen

(english) A first stage in-line water filter for water delivered from the New Blowing Room Pump Room to the Blast Furnace. The strainer contains an electric-driven rotary sieve that catches particulates and prevents them from entering the water system.

Blacking Hole

(english) Irregular-shaped surface cavities in a casting containing carbonaceous matter. Caused by spilling off of the blacking from the mold surface.

battery container

(ไฟฟ้า) เปลือกหม้อแบตเตอรี่, ลักษณะเป็นยางแข็ง หรือส่วนประกอบพลาสติกหล่อเป็นรูปหม้อแบตเตอรี่ตามความต้องการ

Basic Oxygen Furnace (BOF)

(english) "WHAT A pear-shaped furnace, lined with refractory bricks, that refines molten iron from the blast furnace and scrap into steel. Up to 30% of the charge into the BOF can be scrap, with hot metal accounting for the rest. WHY BOFs, which can refine a heat (batch) of steel in less than 45 minutes, replaced open-hearth furnaces in the 1950s; the latter required five to six hours to process the metal. The BOF's rapid operation, lower cost and ease of control give it a distinct advantage over previous methods. HOW Scrap is dumped into the furnace vessel, followed by the hot metal from the blast furnace. A lance is lowered from above, through which blows a high-pressure stream of oxygen to cause chemical reactions that separate impurities as fumes or slag. Once refined, the liquid steel and slag are poured into separate containers. "

Cement Content

(Concrete Engineering) A quantity of cement contained in a unit volume of concrete or mortar, ordinarily expressed as pounds, barrels, or bags per cubic yard.

Mass Curing

(Concrete Engineering) Adiabatic curing, using sealed containers.

Water Vapor Pressure

(Concrete Engineering) The pressure exerted by water vapor. Air that contains higher amounts of water vapor exerts a higher vapor pressure than air which has a lower amount of has a higher water vapor pressure In concrete water vapor pressure is calculated by the difference between the vapor pressure of the concrete and the ambient relative humidity and temperature and in contact with the soil. that is calculated by; based upon relative humidity and temperature. The greater the difference between the water vapor and ambient humidity and temperature, in degrees Fahrenheit. the greater the water vapor pressure exerted.

Basic Oxygen Process 2

(english) A steel making process wherein oxygen of the highest purity is blown onto the surface of a bath of molten iron contained in a basic lined and ladle shaped vessel. The melting cycle duration is extremely short with quality comparable to Open Hearth Steel.

ศัพท์ช่างภาษาอังกฤษ – ไทย จัดกลุ่มตามตัวอักษร A-Z