Bright Dipping

แปลว่า(english) Chemical polishing of aluminum, often by treatment with a mixture of nitric acid and phosphoric acid, yielding a mirror-shiny (specular) highly reflective surface. It is almost always followed by anodizing to protect the surface and provide some choice of color.

AAC - Autoclaved Aerated Concrete

แปลว่า(Concrete Engineering) Exceptionally lightweight precast concrete with high thermal qualities and fire resistence. Suitable for cutting with ordinary hand tools. Mix design is composed of portland cement, sand or siliceous material, lime, gypsum, finely powdered aluminum, and water. Initial mix is a combination of portland cement, sand, lime and gypsum to produce a slurry. Finely powdered aluminum mixed into a paste is added prior to placement into large, rail-like forms. The finely powdered aluminum reacts with the alkaline components of the cement and lime to produce hydrogen gas, which increases the volume approximately five times producing a uniformly, dispersed cellular structure. Units are cut to required shape. Units are placed in an autoclave, an enclosed pressurized chamber, and steam cured at 3500 F. Approximately 80% of the ultimate volume consists of air voids.

Secondary treatment

แปลว่า(Environmental Engineering) In wastewater treatment, the conversion of the suspended, colloidal and dissolved organics remaining after primary treatment into a microbial mass with is then removed in a second sedimentation process. Secondary treatment included both the biological process and the associated sedimentation process.

Blush

แปลว่า(english) A coating defect consisting of the whitening of a cured film which results in a translucent or opaque appearance with accompanying loss of gloss. Blushing usually occurs during the pasteurization or steam processing of films which are undercured or water sensitive.

Brasses

แปลว่า(english) Copper base alloys in which zinc is the principal alloying element. Brass is harder and mechanically stronger than either of its alloying elements copper or zinc. It is formable and ductile; develops high tensile strength with cold-working and is not heat treatable.

Band Saw Steel (Wood)

แปลว่า(english) A hardened tempered bright polished high carbon cold rolled spring steel strip produced especially for use in the manufacture of band saws for sawing wood, non ferrous metals, and plastics. Usually carries some nickel and with a Rockwell value of approximately C40/45.

Blow Back

แปลว่า(english) A coating defect consisting of a lower coating film weight on the bottom of the coated sheet caused by high velocity air in the oven. Blow back usually occurs with high solids coatings which have little solvent to evaporate and "set" the film.

Basic Oxygen Process 2

แปลว่า(english) A steel making process wherein oxygen of the highest purity is blown onto the surface of a bath of molten iron contained in a basic lined and ladle shaped vessel. The melting cycle duration is extremely short with quality comparable to Open Hearth Steel.

GFRC - Glass Fiber Reinforced Concrete

แปลว่า(Concrete Engineering) Concrete panels, usually architectural designs, reinforced with a high zirconia (16% minimum), alkali-resistant glass fiber. Optimum glass fiber content of 5% by weight. Lower fiber content results in lower early ultimate strengths, higher fiber content can produce composite compaction and consolidation difficulties.

Cell

แปลว่า(Environmental Engineering) A unit of varying dimensions in a landfill which is isolated from the environment by 6 to 12 inches of soil cover. A cell is one day's waste or less. A cell is covered with soil at the end of each day.

Modulus of elasticity:

แปลว่า(english) The proportional constant between stress and strain for material with linear elastic behavior: calculated as stress divided by strain. Modulus of elasticity can be interpreted as the slope of the stress-strain graph. It is usually denoted as E, sometimes known as Young's Modulus Y, or E-Modulus.

Billet

แปลว่า(english) (1) A semi-finished section hot rolled from a metal ingot, with a rectangular cross section usually ranging from 16 to 36 in., the width being less than twice the thickness. Where the cross section exceeds 36 in., the term “bloom” is properly but not universally used. Sizes smaller than 16 in. are usually termed “bars”; a solid semi-finished round or square product which has been hot worked by forging, rolling, or extrusion. (2) A semi-finished, cogged, hot rolled or continuous-cast metal product of uniform section, usually rectangular with radiused corners. Billets are relatively larger than bars.