Billet

(english) (1) A semi-finished section hot rolled from a metal ingot, with a rectangular cross section usually ranging from 16 to 36 in., the width being less than twice the thickness. Where the cross section exceeds 36 in., the term “bloom” is properly but not universally used. Sizes smaller than 16 in. are usually termed “bars”; a solid semi-finished round or square product which has been hot worked by forging, rolling, or extrusion. (2) A semi-finished, cogged, hot rolled or continuous-cast metal product of uniform section, usually rectangular with radiused corners. Billets are relatively larger than bars.

Breaker

(english) Uncoiler rolls through which the strip passes; composed of a mandrel and leveling rolls which unwind the strip prior to processing through the Pickler. Breaker rolls assist in breaking up the Hot Mill surface scale.

Backwardation

(english) Market condition where the spot, or current price for a metal is higher than the three-month delivery price. This usually indicates immediate demand is perceived to be stronger than long-term demand. Not considered to be a "normal" market state (See Contango).

Burning

(english) (1) Permanently damaging a metal or alloy by heating to cause either incipient melting or intergranular oxidation. (2) In grinding getting the work hot enough to cause discoloration or to change the microstructure by tempering or hardening.

Blue Annealing

(english) Heating hot rolled ferrous sheet in an open furnace to a temperature within the transformation range and then cooling in air, in order to soften the metal. The formation of a bluish oxide on the surface is incidental.

Bloom 2

(english) A semi-finished hot rolled product, rectangular in cross section, produced on a blooming mill. For iron and steel, the width is not more than twice the thickness, and the cross-sectional area is usually not less than 36 sq. in. Iron and steel blooms are sometimes made by forging.

Aging 1

(english) A change in the properties of certain metal and alloys (such as steel) that occurs at ambient or moderately elevated temperatures after a hot working heat treatment or cold working operation. Typical properties impacted are hardness, yield strength, tensile strength, ductility, impact value, formability, magnetic properties, etc. See also Non-aging.

Blister

(english) 1) Coating defect consisting of the formation of bubbles in a coating, which appear as hemispherical elevations. The blisters are hollow, and are usually caused by entrapped air or solvent. 2) A raised spot on the surface on the surface of metal due to expansion of gas which causes a subsurface metal separation such as inclusions and small laminations.

Blast Furnace

(english) 1) A furnace in which solid fuel (limestone, coke, iron ore) is combined with high-pressure, hot air blast (120,000 psi) to smelt ore in a continuous process (They are never stopped. They can be slowed down or idled). A Blast Furnace in the iron and steel industry is used to produce liquid iron.

Blast Furnace 2

(english) A vertical shaft type smelting furnace in which an air blast is used, usually hot, for producing pih iron. The furnace is continuous in operation using iron ore, coke, and limestone as raw materials which are charged at the top while the molten iron and slag are collected at the bottom and are tapped out at intervals.

Billet 2

(english) A solid semi-finished round or square product that has been hot worked by forging, rolling, or extrusion. An iron or steel billet has a minimum width or thickness of 1 1/2 in. and the cross-sectional area varies from 2 1/4 to 36 sq. in. For nonferrous metals, it may also be a casting suitable for finished or semi-finished rolling or for extrusion.

Basic Oxygen Furnace (BOF)

(english) "WHAT A pear-shaped furnace, lined with refractory bricks, that refines molten iron from the blast furnace and scrap into steel. Up to 30% of the charge into the BOF can be scrap, with hot metal accounting for the rest. WHY BOFs, which can refine a heat (batch) of steel in less than 45 minutes, replaced open-hearth furnaces in the 1950s; the latter required five to six hours to process the metal. The BOF's rapid operation, lower cost and ease of control give it a distinct advantage over previous methods. HOW Scrap is dumped into the furnace vessel, followed by the hot metal from the blast furnace. A lance is lowered from above, through which blows a high-pressure stream of oxygen to cause chemical reactions that separate impurities as fumes or slag. Once refined, the liquid steel and slag are poured into separate containers. "