Yield stress:

แปลว่า(english) A material loaded beyond its yield stress, no longer exhibits linear elastic behavior. Metals, particularly mild steel, generally have a very well defined yield stress compared to other materials. Yield stress is sometimes called yield strength.

Blue Annealing

แปลว่า(english) Heating hot rolled ferrous sheet in an open furnace to a temperature within the transformation range and then cooling in air, in order to soften the metal. The formation of a bluish oxide on the surface is incidental.

Corrosive waste

แปลว่า(Environmental Engineering) A waste that is outside the pH range of 2 to 12.5 or a waste that corrodes steel at a rate greater than 6.35 mm (0.25 in) per year. One of EPA's four hazardous waste properties.

Boron Steels

แปลว่า(english) The addition of boron in the range 0.0005-0.005% to certain steels increases the hardenability. A range of boron steels is now listed in the current BS 970 and are widely used for the production of cold headed fastenings.

Bright Dipping

แปลว่า(english) Chemical polishing of aluminum, often by treatment with a mixture of nitric acid and phosphoric acid, yielding a mirror-shiny (specular) highly reflective surface. It is almost always followed by anodizing to protect the surface and provide some choice of color.

Bearing Strength

แปลว่า(english) The maximum bearing load at failure divided by the effective bearing area. In a pinned or riveted joint, the iffective area is calculated as the product of the diameter of the hole and the thickness of the bearing member.

Biochemical oxygen demand (BOD)

แปลว่า(Environmental Engineering) The amount of oxygen required to oxidize any organic matter present in a water during a specified period of time, usually 5 days. It is an indirect measure of the amount of organic matter present in a water.

Pin support:

แปลว่า(english) In two dimensions, a pin support restrains two translation degrees of freedom but does not restrain rotation. When considering reaction forces, a pin support is usually considered to have two force components: one each about the x and y axes respectively.

AAC - Autoclaved Aerated Concrete

แปลว่า(Concrete Engineering) Exceptionally lightweight precast concrete with high thermal qualities and fire resistence. Suitable for cutting with ordinary hand tools. Mix design is composed of portland cement, sand or siliceous material, lime, gypsum, finely powdered aluminum, and water. Initial mix is a combination of portland cement, sand, lime and gypsum to produce a slurry. Finely powdered aluminum mixed into a paste is added prior to placement into large, rail-like forms. The finely powdered aluminum reacts with the alkaline components of the cement and lime to produce hydrogen gas, which increases the volume approximately five times producing a uniformly, dispersed cellular structure. Units are cut to required shape. Units are placed in an autoclave, an enclosed pressurized chamber, and steam cured at 3500 F. Approximately 80% of the ultimate volume consists of air voids.

Balanced Steel

แปลว่า(english) Steels in which the deoxidisation is controlled to produce an intermediate structure between a rimmed and killed steel, Sometimes referred to as semi-killed steels, they possess uniform properties throughout the ingot and amongst their applications are boiler plate and structural sections.

Secondary treatment

แปลว่า(Environmental Engineering) In wastewater treatment, the conversion of the suspended, colloidal and dissolved organics remaining after primary treatment into a microbial mass with is then removed in a second sedimentation process. Secondary treatment included both the biological process and the associated sedimentation process.

Hydrogenesis

แปลว่า(Concrete Engineering) Another term for condensation. The term is especially applied to base and soil substrates under highway pavements. where the barometric pump causes the inhalation of humid air, which then condenses in those structures, causing an ever increasing moisture content and sometimes instability.