In situ treatment

(Environmental Engineering) Treatment of a waste in place, as opposed to pumping or digging the waste up and then treating it.

Baked Strength

(english) Compressive, shear, tensile or transverse strength of a mold sand mixture when baked at a temperature above 231 B0F (111 B0C) and then cooled to room temperature.

Tilt-up

(Concrete Engineering) A method of concrete construction such as where members are cast horizontally near their eventual position, usually on a recently placed slab, and then tilted into place after removal of forms.

Blue Annealing

(english) Heating hot rolled ferrous sheet in an open furnace to a temperature within the transformation range and then cooling in air, in order to soften the metal. The formation of a bluish oxide on the surface is incidental.

Secondary treatment

(Environmental Engineering) In wastewater treatment, the conversion of the suspended, colloidal and dissolved organics remaining after primary treatment into a microbial mass with is then removed in a second sedimentation process. Secondary treatment included both the biological process and the associated sedimentation process.

Hydrogenesis

(Concrete Engineering) Another term for condensation. The term is especially applied to base and soil substrates under highway pavements. where the barometric pump causes the inhalation of humid air, which then condenses in those structures, causing an ever increasing moisture content and sometimes instability.

Nitrification

(Environmental Engineering) The biological oxidation of ammonia and ammonium sequentially to nitrite and then nitrate. It occurs naturally in surface waters, and can be engineered in wastewater treatment systems. The purpose of nitrification in wastewater treatment systems is a reduction in the oxygen demand resulting from the ammonia.

Box Annealing 2

(english) A process of annealing a ferrous alloy in a closed metal container, with or without packing materials, in order to minimize the effects of oxidation. The charge is normally heated slowly to a temperature below the transformation range, but occasionally above or within it, and then is slowly cooled.

Toxicity

(Environmental Engineering) A U.S. EPA hazardous waste characteristic defined with a rigorous test procedure, the TCLP (for Toxicity Characteristic Leaching Procedure). In the procedure, a waste is extracted for 24 hours with an acetic acid solution. The acid extract is then analyzed for the presence of any of the contaminants listed in the procedure.

Box Annealing

(english) Annealing a metal or alloy in a sealed container under conditions that minimize oxidation. In box annealing a ferrous alloy, the charge is usually heated slowly to a temperature below the transformation range, but sometimes above or within it, and is then cooled slowly; this process is also called close annealing or pot annealing.

Brinell Hardness Test

(english) A common standard method of measuring the hardness of materials. The smooth surface of the metal is subjected to indentation by a hardened steel ball under pressure. The diameter of the indentation, in the material surface, is then measured by a microscope and the hardness value is read from a chart or determined by a prescribed formula.

Brazing

(english) Joining metals by fusion of nonferrous alloys that have melting points above 800 F (425C), but lower than those of the metals being joined. May be accomplished by a torch. Filler metal is ordinarily in rod form in torch brazing; whereas in furnace and dip brazing the work material is first assembled and the filler metal may then be applied as wire, washers, clips, bands, or may be bonded, as in brazing sheet.