Baked Strength

แปลว่า(english) Compressive, shear, tensile or transverse strength of a mold sand mixture when baked at a temperature above 231 B0F (111 B0C) and then cooled to room temperature.

Portland-Pozzolan Cement (ASTM C 595)

แปลว่า(Concrete Engineering) The product obtained by intimately intergrinding a mixture of portland-cement clinker and pozzolan, or an intimate and uniform blend of portland cement and fine pozzolan.

Calcium Aluminate Cement

แปลว่า(Concrete Engineering) The product obtained by pulverizing clinker consisting essentially of hydraulic calcium aluminates resulting from fusing or sintering a suitable proportioned mixture of aluminous and calcareous materials.

Sacking

แปลว่า(Concrete Engineering) Removing or alleviating defects on a concrete surface by applying a mixture of sand and cement to the moistened surface and rubbing with a coarse material such as burlap.

Cement, Portland (ASTM C150) (Concrete Engineering)

แปลว่าA powdery substance made by burning, at a high temperature, a mixture of clay and limestone producing lumps called “clinkers” which are ground into a fine powder consisting of hydraulic calcium silicates. For non-portland cements, see aluminous cement.

Bright Dipping

แปลว่า(english) Chemical polishing of aluminum, often by treatment with a mixture of nitric acid and phosphoric acid, yielding a mirror-shiny (specular) highly reflective surface. It is almost always followed by anodizing to protect the surface and provide some choice of color.

Pumping (of Pavements)

แปลว่า(Concrete Engineering) The ejection of a mixture of water and solid materials such as clay or silt along cracks, transverse or longitudinal joints, and along pavement edges caused by downward slab movement due to the passage of heavy loads, machinery or equipment over the pavement after free water has accumulated in or on the subbase, subgrade or basecourse.

Blast Furnace Slag

แปลว่า(Concrete Engineering) A non-metallic waste product developed in the manufacture of pig iron, consisting basically of a mixture of lime, silica and alumina, the same oxides that make up portland cement, but not in the same proportions or forms. It is used both in the manufacture of portland blast furnace slag cement and as an aggregate for lightweight concrete.