Blue Annealing

แปลว่า(english) Heating hot rolled ferrous sheet in an open furnace to a temperature within the transformation range and then cooling in air, in order to soften the metal. The formation of a bluish oxide on the surface is incidental.

Aging 1

แปลว่า(english) A change in the properties of certain metal and alloys (such as steel) that occurs at ambient or moderately elevated temperatures after a hot working heat treatment or cold working operation. Typical properties impacted are hardness, yield strength, tensile strength, ductility, impact value, formability, magnetic properties, etc. See also Non-aging.

Bloom 2

แปลว่า(english) A semi-finished hot rolled product, rectangular in cross section, produced on a blooming mill. For iron and steel, the width is not more than twice the thickness, and the cross-sectional area is usually not less than 36 sq. in. Iron and steel blooms are sometimes made by forging.

Blast Furnace 2

แปลว่า(english) A vertical shaft type smelting furnace in which an air blast is used, usually hot, for producing pih iron. The furnace is continuous in operation using iron ore, coke, and limestone as raw materials which are charged at the top while the molten iron and slag are collected at the bottom and are tapped out at intervals.

Blast Furnace

แปลว่า(english) 1) A furnace in which solid fuel (limestone, coke, iron ore) is combined with high-pressure, hot air blast (120,000 psi) to smelt ore in a continuous process (They are never stopped. They can be slowed down or idled). A Blast Furnace in the iron and steel industry is used to produce liquid iron.

Billet 2

แปลว่า(english) A solid semi-finished round or square product that has been hot worked by forging, rolling, or extrusion. An iron or steel billet has a minimum width or thickness of 1 1/2 in. and the cross-sectional area varies from 2 1/4 to 36 sq. in. For nonferrous metals, it may also be a casting suitable for finished or semi-finished rolling or for extrusion.

Basic Oxygen Furnace (BOF)

แปลว่า(english) "WHAT A pear-shaped furnace, lined with refractory bricks, that refines molten iron from the blast furnace and scrap into steel. Up to 30% of the charge into the BOF can be scrap, with hot metal accounting for the rest. WHY BOFs, which can refine a heat (batch) of steel in less than 45 minutes, replaced open-hearth furnaces in the 1950s; the latter required five to six hours to process the metal. The BOF's rapid operation, lower cost and ease of control give it a distinct advantage over previous methods. HOW Scrap is dumped into the furnace vessel, followed by the hot metal from the blast furnace. A lance is lowered from above, through which blows a high-pressure stream of oxygen to cause chemical reactions that separate impurities as fumes or slag. Once refined, the liquid steel and slag are poured into separate containers. "

Aging 2

แปลว่า(english) A change in properties that occurs at ambient or moderately elevated temperatures after hot working or a heat treating operation (quench aging in ferrous alloys), or after a cold working operation (strain aging). The change in properties is often, but not always, due to a phase change (precipitation), but does not involve a change in chemical composition. In a metal or alloy, a change in properties that generally occurs slowly at room temperature and more rapidly at higher temperatures.

Agglomerating Processes

แปลว่า(english) "Fine particles of limestone (flux) and iron ore are difficult to handle and transport because of dusting and decomposition, so the powdery material usually is processed into larger pieces. The raw material's properties determine the technique that is used by mills. 1) SINTER Baked particles that stick together in roughly one-inch chunks. Normally used for iron ore dust collected from the blast furnaces. 2) PELLETS Iron ore or limestone particles are rolled into little balls in a balling drum and hardened by heat. 3) BRIQUETTES Small lumps are formed by pressing material together. Hot Iron Briquetting (HBI) is a concentrated iron ore substitute for scrap for use in electric furnaces.

Black Plate

แปลว่า(english) A light weight or a thin uncoated steel sheet or strip so called because of its dark oxide coloring prior to pickling. It is manufactured by two different processes. (1) Form sheet bar on single stand sheet mills or sheet mills in tandem. This method is now almost obsolete. (2) On modern, high speed continuous tandem cold reduction mills from coiled hot rolled pickled wide strip into ribbon wound coils to finished gage. Sizes range from 12 to 32 in width, and in thicknesses from 55 lbs. to 275 lbs. base box weight. It is used either as is for stampings, or may be enameled or painted or tin or terne coated.