Band Saw Steel (Wood)

แปลว่า(english) A hardened tempered bright polished high carbon cold rolled spring steel strip produced especially for use in the manufacture of band saws for sawing wood, non ferrous metals, and plastics. Usually carries some nickel and with a Rockwell value of approximately C40/45.

Bridling

แปลว่า(english) The cold working of dead soft annealed strip metal immediately prior to a forming, bending, or drawing operation. A process designed to prevent the formulation of Luder's lines. Caution-Bridled metal should be used promptly and not permitted to (of itself) return to its pre-bridled condition.

Burr

แปลว่า(english) The very subtle ridge on the edge of strip steel left by cutting operations such as slitting, trimming, shearing, or blanking. For example, as a steel processor trims the sides of the sheet steel parallel or cuts a sheet of steel into strips, its edges will bend with the direction of the cut.

Black Plate

แปลว่า(english) A light weight or a thin uncoated steel sheet or strip so called because of its dark oxide coloring prior to pickling. It is manufactured by two different processes. (1) Form sheet bar on single stand sheet mills or sheet mills in tandem. This method is now almost obsolete. (2) On modern, high speed continuous tandem cold reduction mills from coiled hot rolled pickled wide strip into ribbon wound coils to finished gage. Sizes range from 12 to 32 in width, and in thicknesses from 55 lbs. to 275 lbs. base box weight. It is used either as is for stampings, or may be enameled or painted or tin or terne coated.

Break Test (for tempered steel)

แปลว่า(english) A method of testing hardened and tempered high carbon spring steel strip wherein the specimen is held and bent across the grain in a vice-like calibrated testing machine. Pressure is applied until the metal fractures at which point a reading is taken and compared with a standard chart of brake limitations for various thickness ranges.

Bainite

แปลว่า(english) A eutectoid transformation product of ferrite and a fine dispersion of carbide, generally formed at temperatures below 840 to 930 F (450 to 500 C): upper bainite is an aggregate containing parallel lath-shape units of ferrite, produces the so-called feathery appearance in optical microscopy, and is formed at temperatures above about 660 F (350 C); lower bainite consists of individual plate-shape units and is formed at temperatures below about 660 F (350 C). Also, a slender, needle-like (acicular) microstructure appearing in spring steel strip characterized by toughness and greater ductility than tempered Martensite. Bainite is a decomposition product of Austenite best developed at interrupted holding temperatures below those forming fine pearlite and above those giving Martensite.