Blue Annealing

แปลว่า(english) Heating hot rolled ferrous sheet in an open furnace to a temperature within the transformation range and then cooling in air, in order to soften the metal. The formation of a bluish oxide on the surface is incidental.

Hydrogenesis

แปลว่า(Concrete Engineering) Another term for condensation. The term is especially applied to base and soil substrates under highway pavements. where the barometric pump causes the inhalation of humid air, which then condenses in those structures, causing an ever increasing moisture content and sometimes instability.

Blow Back

แปลว่า(english) A coating defect consisting of a lower coating film weight on the bottom of the coated sheet caused by high velocity air in the oven. Blow back usually occurs with high solids coatings which have little solvent to evaporate and "set" the film.

Water Vapor Pressure

แปลว่า(Concrete Engineering) The pressure exerted by water vapor. Air that contains higher amounts of water vapor exerts a higher vapor pressure than air which has a lower amount of has a higher water vapor pressure In concrete water vapor pressure is calculated by the difference between the vapor pressure of the concrete and the ambient relative humidity and temperature and in contact with the soil. that is calculated by; based upon relative humidity and temperature. The greater the difference between the water vapor and ambient humidity and temperature, in degrees Fahrenheit. the greater the water vapor pressure exerted.

Blast Furnace

แปลว่า(english) 1) A furnace in which solid fuel (limestone, coke, iron ore) is combined with high-pressure, hot air blast (120,000 psi) to smelt ore in a continuous process (They are never stopped. They can be slowed down or idled). A Blast Furnace in the iron and steel industry is used to produce liquid iron.

Blasting (Blast Cleaning)

แปลว่า(english) A process for cleaning or finishing metal objects by use of an air blast or centrifugal wheel that throws abrasive particles against the surface of the work pieces. Small, irregular particles of steel or iron are used as the abrasive in grit blasting, and steel or iron balls in shot blasting.

Blast Furnace 2

แปลว่า(english) A vertical shaft type smelting furnace in which an air blast is used, usually hot, for producing pih iron. The furnace is continuous in operation using iron ore, coke, and limestone as raw materials which are charged at the top while the molten iron and slag are collected at the bottom and are tapped out at intervals.

AAC - Autoclaved Aerated Concrete

แปลว่า(Concrete Engineering) Exceptionally lightweight precast concrete with high thermal qualities and fire resistence. Suitable for cutting with ordinary hand tools. Mix design is composed of portland cement, sand or siliceous material, lime, gypsum, finely powdered aluminum, and water. Initial mix is a combination of portland cement, sand, lime and gypsum to produce a slurry. Finely powdered aluminum mixed into a paste is added prior to placement into large, rail-like forms. The finely powdered aluminum reacts with the alkaline components of the cement and lime to produce hydrogen gas, which increases the volume approximately five times producing a uniformly, dispersed cellular structure. Units are cut to required shape. Units are placed in an autoclave, an enclosed pressurized chamber, and steam cured at 3500 F. Approximately 80% of the ultimate volume consists of air voids.