Bleeder

แปลว่า(english) A defect wherein a casting lacks completeness due to moltn metal draining or leaking out of some part of the mold cavity after pouraing has stopped.

Baked Strength

แปลว่า(english) Compressive, shear, tensile or transverse strength of a mold sand mixture when baked at a temperature above 231 B0F (111 B0C) and then cooled to room temperature.

Consolidation

แปลว่า(Concrete Engineering) Compaction usually accomplished by vibration of newly placed concrete to minimum practical volume, to mold it within form shapes and around embedded parts and reinforcement, and to eliminate voids other than entrained air.

A Elevation

แปลว่า(English) The top level of the boiler firebox where four oil guns are located. The oil guns are used to produce steam and maintain pressure while the boiler is on oil fire.

nip

Back-up Roll

แปลว่า(english) 1) Roll used as a support roll mainly for plater rolls. 2) Two rolls, one on top and one on bottom of the two work rolls which apply pressure and reduce the flexing of the work rolls.

Dry Rodded Weight

แปลว่า(Concrete Engineering) The weight of dry aggregate rodded into a cylindrical container of diameter approximately equal to the height, each of 3 layers rodded 25 times, and the excess aggregate struck off level with the top of the container

Slip Form

แปลว่า(Concrete Engineering) A form which is raised or pulled as concrete is placed; may move vertically to form wails, stacks, bins or silos, usually of uniform cross section from bottom to top; or a generally horizontal direction to lay concrete evenly for highways, on slopes and inverts of canals, tunnels, and siphons.

Blast Furnace 2

แปลว่า(english) A vertical shaft type smelting furnace in which an air blast is used, usually hot, for producing pih iron. The furnace is continuous in operation using iron ore, coke, and limestone as raw materials which are charged at the top while the molten iron and slag are collected at the bottom and are tapped out at intervals.

Carbonation

แปลว่า(Concrete Engineering) 1) Reaction between the products of portland cement (soluble calcium hydroxides), water and carbon dioxide to produce insoluble calcium carbonate (efflorescence). 2) Soft white, chalky surface dusting of freshly placed, unhardened concrete caused by carbon dioxide from unvented heaters or gasoline powered equipment in an enclosed space. 3) Carbonated, dense, impermeable to absorption, top layer of the surface of concrete caused by surface reaction to carbon dioxide. This carbonated layer becomes denser and deeper over a period of time. 4) Reaction with carbon dioxide which produces a slight shrinkage in concrete. Improves chemical stability. Concrete masonry units during manufacturing may be deliberately exposed to carbon dioxide after reaching 80% strength to induce carbonation shrinkage to make the units more dimensionally stable. Future drying shrinkage is reduced by as much as 30%.