Busheling

แปลว่า(english) A widely traded form of steel scrap consisting of sheet clips and stampings from metal production. Bushel baskets were used to collect the material through World War II, giving rise to the term.

Bake Hardenable Steel

แปลว่า(english) A cold-rolled, low-carbon sheet steel used for automotive body panel applications. Because of the steel’s special processing, it has good stamping and strength characteristics and after paint is baked on, improved dent resistance.

Blue Annealing

แปลว่า(english) Heating hot rolled ferrous sheet in an open furnace to a temperature within the transformation range and then cooling in air, in order to soften the metal. The formation of a bluish oxide on the surface is incidental.

Blow Back

แปลว่า(english) A coating defect consisting of a lower coating film weight on the bottom of the coated sheet caused by high velocity air in the oven. Blow back usually occurs with high solids coatings which have little solvent to evaporate and "set" the film.

Blanking

แปลว่า(english) An early step in preparing flat-rolled steel for use by an end user. A blank is a section of sheet that has the same outer dimensions as a specified part (such as a car door or hood) but that has not yet been stamped. Steel processors may offer blanking for their customers to reduce their labor and transportation costs; excess steel can be trimmed prior to shipment.

Brazing

แปลว่า(english) Joining metals by fusion of nonferrous alloys that have melting points above 800 F (425C), but lower than those of the metals being joined. May be accomplished by a torch. Filler metal is ordinarily in rod form in torch brazing; whereas in furnace and dip brazing the work material is first assembled and the filler metal may then be applied as wire, washers, clips, bands, or may be bonded, as in brazing sheet.

Zinc

แปลว่า(english) Chemical Symbol Zn. Element No. 30 of the periodic system; atomic weight 65.38. Blue-white metal; when pure, malleable and ductile even at ordinary temperatures; melting point 787 (degrees) F.; boiling point 1665 (degrees) F., specific gravity 7.14. Can be electrodeposited; it is extensively used as a coating for steel and sheet zinc finds many outlets, such as dry batteries, etc. Zinc-base alloys are of great importance in die casting. Its most important alloy is brass.

Batch Anneal

แปลว่า(english) The process by which a large, stationary stack of steel coils (4 coils high) is subjected to a long heat-treating cycle. This process enables the cold-rolled sheet to fully recrystallize into the softest possible product conforming to customer specifications. Controlling the recrystallization process makes a fine-grained microstructure easy to obtain, and minimizes the tendencies for retention of directional properties of the rolled steel which could produce undesirable shapes in the stamping of a cylindrical part such as a can. Also see Anneal and Continuous Anneal.

Brown Sharp Gages

แปลว่า(english) A standard series of sizes refered to by numbers, in which the diameter of wire or thickness of sheet metal is generally produced and which is used in the manufacture of brass, bronze, copper, copper-base alloys and aluminum. These gage numbers have a definite relationship to each other. In this system, the decimal thickness is reduced by 50% every six gage numbers- while temper is expressed by the number of B&S gage numbers as cold reduced in thickness from previous annealing. For each B&S gage number in thickness reduction, where is assigned a hardness value of 1/4 hard.