Temperature Rise

แปลว่า(Concrete Engineering) The increase of concrete temperature caused by heat of hydration and heat from other sources.

Adsorption Water

แปลว่า(Concrete Engineering) Water held on surfaces in a material by either physical and/or chemical forces.

Dry Rodded Weight

แปลว่า(Concrete Engineering) The weight of dry aggregate rodded into a cylindrical container of diameter approximately equal to the height, each of 3 layers rodded 25 times, and the excess aggregate struck off level with the top of the container

HRM High Reactivity Metakaolin

แปลว่า(Concrete Engineering) Refined form of an ASTM C618, Class N (natural) pozzolan. A high performance, mineral admixture, similar in performance to silica fume, additionally comparable in cost. Pure white powdered in form will, not effect the natural color or darken concrete as silica fume does. Suitable for high-performance color matching in architectural concrete. Dosage at 5% to 10%, of cement by weight. No bleed water, better finishability, more creamy, cleanup is easier with slightly higher 28 day strengths and 25% - 35% less plasticizer is required than silica fume.

Plane of Weakness

แปลว่า(Concrete Engineering) The plane along which a structure under stress will tend to fracture; may exist because of the nature of the structure and its loading, by accident, or by design.

AAC - Autoclaved Aerated Concrete

แปลว่า(Concrete Engineering) Exceptionally lightweight precast concrete with high thermal qualities and fire resistence. Suitable for cutting with ordinary hand tools. Mix design is composed of portland cement, sand or siliceous material, lime, gypsum, finely powdered aluminum, and water. Initial mix is a combination of portland cement, sand, lime and gypsum to produce a slurry. Finely powdered aluminum mixed into a paste is added prior to placement into large, rail-like forms. The finely powdered aluminum reacts with the alkaline components of the cement and lime to produce hydrogen gas, which increases the volume approximately five times producing a uniformly, dispersed cellular structure. Units are cut to required shape. Units are placed in an autoclave, an enclosed pressurized chamber, and steam cured at 3500 F. Approximately 80% of the ultimate volume consists of air voids.

Cement Content

แปลว่า(Concrete Engineering) A quantity of cement contained in a unit volume of concrete or mortar, ordinarily expressed as pounds, barrels, or bags per cubic yard.

Mass Curing

แปลว่า(Concrete Engineering) Adiabatic curing, using sealed containers.

Water Vapor Pressure

แปลว่า(Concrete Engineering) The pressure exerted by water vapor. Air that contains higher amounts of water vapor exerts a higher vapor pressure than air which has a lower amount of has a higher water vapor pressure In concrete water vapor pressure is calculated by the difference between the vapor pressure of the concrete and the ambient relative humidity and temperature and in contact with the soil. that is calculated by; based upon relative humidity and temperature. The greater the difference between the water vapor and ambient humidity and temperature, in degrees Fahrenheit. the greater the water vapor pressure exerted.

Neat Cement-Paste

แปลว่า(Concrete Engineering) A mixture of water and hydraulic cement, both before and after setting and hardening.

Saponification

แปลว่า(Concrete Engineering) The deposit of a gray scum or gray dust on the inside surface of a subgrade wall or floor; as the result of moisture moving through the concrete and washing certain chemicals from the concrete mass.

Cementitious

แปลว่า(Concrete Engineering) Having cement-like, cementing, or bonding type properties. Material or substance producing bonding properties or cement-like materials.