Absorbed Moisture

แปลว่า(Concrete Engineering) Moisture which is mechanically held in a material. In aggregates, that water which is not available to become part of the mixing water is designated "absorbed" water.

Base Metal

แปลว่า(english) (1) The metal present in the largest proportion in an alloy; (2) the metal to be brazed, cut or welded; (3) after welding the part of the metal that was not melted during the process.

Chlorofluorocarbons

แปลว่า(Environmental Engineering) Synthetic organic compounds used for refrigerants, aerosol propellants (prohibited in the U.S.), and blowing agents in plastic foams. CFCs migrate to the upper atmosphere destroying ozone and increasing global warming. Typical atmospheric residence times are 50 to 200 years.

Brinell Hardness

แปลว่า(english) The hardness of a metal or part, as represented by the number obtained from the ratio between the load applied on the spherical area of the impression made by a steel ball forced into the surface of the material tested.

Backer (back-up plate)

แปลว่า(english) A “tool” or reinforcing part, which presses against the outer surface of an extrusion die, supporting it against the pressure of the extruding metal. The backer has an opening larger than the die aperture, allowing the extruded product to emerge without marring its soft surface.

Blanking

แปลว่า(english) An early step in preparing flat-rolled steel for use by an end user. A blank is a section of sheet that has the same outer dimensions as a specified part (such as a car door or hood) but that has not yet been stamped. Steel processors may offer blanking for their customers to reduce their labor and transportation costs; excess steel can be trimmed prior to shipment.

Batch Anneal

แปลว่า(english) The process by which a large, stationary stack of steel coils (4 coils high) is subjected to a long heat-treating cycle. This process enables the cold-rolled sheet to fully recrystallize into the softest possible product conforming to customer specifications. Controlling the recrystallization process makes a fine-grained microstructure easy to obtain, and minimizes the tendencies for retention of directional properties of the rolled steel which could produce undesirable shapes in the stamping of a cylindrical part such as a can. Also see Anneal and Continuous Anneal.

Bainite

แปลว่า(english) A eutectoid transformation product of ferrite and a fine dispersion of carbide, generally formed at temperatures below 840 to 930 F (450 to 500 C): upper bainite is an aggregate containing parallel lath-shape units of ferrite, produces the so-called feathery appearance in optical microscopy, and is formed at temperatures above about 660 F (350 C); lower bainite consists of individual plate-shape units and is formed at temperatures below about 660 F (350 C). Also, a slender, needle-like (acicular) microstructure appearing in spring steel strip characterized by toughness and greater ductility than tempered Martensite. Bainite is a decomposition product of Austenite best developed at interrupted holding temperatures below those forming fine pearlite and above those giving Martensite.