Impermeable

แปลว่า(Concrete Engineering) The ability of a material or product to reduce or eliminate gaseous transmissions through it's mass; measured as the rate of Water Vapor Transmission (WVT). Note: Not all materials that are waterproof are vaporproof; all materials that are vaporproof are inherently waterproof.

Mixing Speed

แปลว่า(Concrete Engineering) Rate of mixer drum rotation or that of the paddles in a pan, open-top, or trough type mixer, when mixing a batch; expressed in revolutions per minute (rpm) or in peripheral] feet per minute of A point on the circumference at maximum diameter.

Box Annealing

แปลว่า(english) Annealing a metal or alloy in a sealed container under conditions that minimize oxidation. In box annealing a ferrous alloy, the charge is usually heated slowly to a temperature below the transformation range, but sometimes above or within it, and is then cooled slowly; this process is also called close annealing or pot annealing.

Box Annealing 2

แปลว่า(english) A process of annealing a ferrous alloy in a closed metal container, with or without packing materials, in order to minimize the effects of oxidation. The charge is normally heated slowly to a temperature below the transformation range, but occasionally above or within it, and then is slowly cooled.

Bainite

แปลว่า(english) A eutectoid transformation product of ferrite and a fine dispersion of carbide, generally formed at temperatures below 840 to 930 F (450 to 500 C): upper bainite is an aggregate containing parallel lath-shape units of ferrite, produces the so-called feathery appearance in optical microscopy, and is formed at temperatures above about 660 F (350 C); lower bainite consists of individual plate-shape units and is formed at temperatures below about 660 F (350 C). Also, a slender, needle-like (acicular) microstructure appearing in spring steel strip characterized by toughness and greater ductility than tempered Martensite. Bainite is a decomposition product of Austenite best developed at interrupted holding temperatures below those forming fine pearlite and above those giving Martensite.

Brazing

แปลว่า(english) Joining metals by fusion of nonferrous alloys that have melting points above 800 F (425C), but lower than those of the metals being joined. May be accomplished by a torch. Filler metal is ordinarily in rod form in torch brazing; whereas in furnace and dip brazing the work material is first assembled and the filler metal may then be applied as wire, washers, clips, bands, or may be bonded, as in brazing sheet.

Basic Oxygen Furnace (BOF)

แปลว่า(english) "WHAT A pear-shaped furnace, lined with refractory bricks, that refines molten iron from the blast furnace and scrap into steel. Up to 30% of the charge into the BOF can be scrap, with hot metal accounting for the rest. WHY BOFs, which can refine a heat (batch) of steel in less than 45 minutes, replaced open-hearth furnaces in the 1950s; the latter required five to six hours to process the metal. The BOF's rapid operation, lower cost and ease of control give it a distinct advantage over previous methods. HOW Scrap is dumped into the furnace vessel, followed by the hot metal from the blast furnace. A lance is lowered from above, through which blows a high-pressure stream of oxygen to cause chemical reactions that separate impurities as fumes or slag. Once refined, the liquid steel and slag are poured into separate containers. "