Bend Test

แปลว่า(english) Various tests which is used to ascertain the toughness and ductility of a metal product, in which the material is bent around its axis and/ or around an outside radius. A complete test might specify such a bend to be both with and against the direction of grain. For testing, samples should be edge filed to remove burrs and any edgewise cracks resulting from slitting or shearing. If a vice is to be employed, then you must line the jaws with some soft metal, to permit a flow of the metal in the piece being tested.

Busheling

แปลว่า(english) A widely traded form of steel scrap consisting of sheet clips and stampings from metal production. Bushel baskets were used to collect the material through World War II, giving rise to the term.

Blast Cleaning (blasting)

แปลว่า(english) A process for cleaning or finishing metal objects by use of an air jet or centrifugal wheel that propels abrasive particles (grit, sand, or shot) against the surfaces of the workpiece at high velocity.

Bottle Top Mold

แปลว่า(english) Ingot mold, with the top constricted; used in the manufacture of capped steel, the metal in the constriction being covered with a cap fitting into the bottle-neck, which stops rimming action by trapping escaping gases.

Slump Cone

แปลว่า(Concrete Engineering) A metal mold in the form of a truncated cone with a top diameter of 4”, a bottom diameter of 8”, and a height of 12”, used to fabricate the specimen for a slump test.

Brazing

แปลว่า(english) Joining metals by fusion of nonferrous alloys that have melting points above 800 F (425C), but lower than those of the metals being joined. May be accomplished by a torch. Filler metal is ordinarily in rod form in torch brazing; whereas in furnace and dip brazing the work material is first assembled and the filler metal may then be applied as wire, washers, clips, bands, or may be bonded, as in brazing sheet.

Blue Annealing

แปลว่า(english) Heating hot rolled ferrous sheet in an open furnace to a temperature within the transformation range and then cooling in air, in order to soften the metal. The formation of a bluish oxide on the surface is incidental.

Burning

แปลว่า(english) (1) Permanently damaging a metal or alloy by heating to cause either incipient melting or intergranular oxidation. (2) In grinding getting the work hot enough to cause discoloration or to change the microstructure by tempering or hardening.

Brinell Hardness

แปลว่า(english) The hardness of a metal or part, as represented by the number obtained from the ratio between the load applied on the spherical area of the impression made by a steel ball forced into the surface of the material tested.

Backwardation

แปลว่า(english) Market condition where the spot, or current price for a metal is higher than the three-month delivery price. This usually indicates immediate demand is perceived to be stronger than long-term demand. Not considered to be a "normal" market state (See Contango).

Brinell Hardness Number

แปลว่า(english) The value of hardness of a metal on an arbitrary scale representing kg/mm2, determined by measuring the diameter of the impression made by a ball of given diameter applied under a known load. Values are expressed in Brinell Hardness Numbers, BHN

Backer (back-up plate)

แปลว่า(english) A “tool” or reinforcing part, which presses against the outer surface of an extrusion die, supporting it against the pressure of the extruding metal. The backer has an opening larger than the die aperture, allowing the extruded product to emerge without marring its soft surface.