แปลว่า(english) 1) Wooden separators which are used at both the bottom of a lift and between IPM's (bundles) of a lift. 2) The act of placing 4x4s between the lifts in the piler's box.

BREATHER

แปลว่า(english) A device which permits air to move in and out of a container or component to maintain atmospheric pressure.

Reversible reaction

แปลว่า(Environmental Engineering) A reaction in which the reactant(s) proceed to product(s), but the products react at an appreciable rate to reform reactant(s).

Blank 2

แปลว่า(english) A piece of stock (also call a “slug” or “multiple”) from which a forging is to be made.

Wetland

แปลว่า(Environmental Engineering) Semi-aquatic land, that is land that is either inundated or saturated by water for varying periods of time during each year, and that supports aquatic vegetation which is specifically adapted for saturated soil conditions.

Heterotrophic

แปลว่า(Environmental Engineering) A group of organisms which obtain carbon for synthesis from other organic matter or proteins.

Plane of Weakness

แปลว่า(Concrete Engineering) The plane along which a structure under stress will tend to fracture; may exist because of the nature of the structure and its loading, by accident, or by design.

Blow Back

แปลว่า(english) A coating defect consisting of a lower coating film weight on the bottom of the coated sheet caused by high velocity air in the oven. Blow back usually occurs with high solids coatings which have little solvent to evaporate and "set" the film.

Stiffness:

แปลว่า(english) This is a general term which may be applied to materials or structures. When a force is applied to a structure, there is a displacement in the direction of the force; stiffness is the ratio of the force divided by the displacement. High stiffness means that a large force produces a small displacement. When discussing the stiffness of a material, the concept is the same, except that stress substitutes for force, and strain substitutes for displacement; see modulus of elasticity.

Brasses

แปลว่า(english) Copper base alloys in which zinc is the principal alloying element. Brass is harder and mechanically stronger than either of its alloying elements copper or zinc. It is formable and ductile; develops high tensile strength with cold-working and is not heat treatable.

Basic Oxygen Furnace (BOF)

แปลว่า(english) "WHAT A pear-shaped furnace, lined with refractory bricks, that refines molten iron from the blast furnace and scrap into steel. Up to 30% of the charge into the BOF can be scrap, with hot metal accounting for the rest. WHY BOFs, which can refine a heat (batch) of steel in less than 45 minutes, replaced open-hearth furnaces in the 1950s; the latter required five to six hours to process the metal. The BOF's rapid operation, lower cost and ease of control give it a distinct advantage over previous methods. HOW Scrap is dumped into the furnace vessel, followed by the hot metal from the blast furnace. A lance is lowered from above, through which blows a high-pressure stream of oxygen to cause chemical reactions that separate impurities as fumes or slag. Once refined, the liquid steel and slag are poured into separate containers. "

AAC - Autoclaved Aerated Concrete

แปลว่า(Concrete Engineering) Exceptionally lightweight precast concrete with high thermal qualities and fire resistence. Suitable for cutting with ordinary hand tools. Mix design is composed of portland cement, sand or siliceous material, lime, gypsum, finely powdered aluminum, and water. Initial mix is a combination of portland cement, sand, lime and gypsum to produce a slurry. Finely powdered aluminum mixed into a paste is added prior to placement into large, rail-like forms. The finely powdered aluminum reacts with the alkaline components of the cement and lime to produce hydrogen gas, which increases the volume approximately five times producing a uniformly, dispersed cellular structure. Units are cut to required shape. Units are placed in an autoclave, an enclosed pressurized chamber, and steam cured at 3500 F. Approximately 80% of the ultimate volume consists of air voids.