ผลการค้นหา

Batch Anneal

แปลว่า(english) The process by which a large, stationary stack of steel coils (4 coils high) is subjected to a long heat-treating cycle. This process enables the cold-rolled sheet to fully recrystallize into the softest possible product conforming to customer specifications. Controlling the recrystallization process makes a fine-grained microstructure easy to obtain, and minimizes the tendencies for retention of directional properties of the rolled steel which could produce undesirable shapes in the stamping of a cylindrical part such as a can. Also see Anneal and Continuous Anneal.

Stiffness:

แปลว่า(english) This is a general term which may be applied to materials or structures. When a force is applied to a structure, there is a displacement in the direction of the force; stiffness is the ratio of the force divided by the displacement. High stiffness means that a large force produces a small displacement. When discussing the stiffness of a material, the concept is the same, except that stress substitutes for force, and strain substitutes for displacement; see modulus of elasticity.

Bainite

แปลว่า(english) A eutectoid transformation product of ferrite and a fine dispersion of carbide, generally formed at temperatures below 840 to 930 F (450 to 500 C): upper bainite is an aggregate containing parallel lath-shape units of ferrite, produces the so-called feathery appearance in optical microscopy, and is formed at temperatures above about 660 F (350 C); lower bainite consists of individual plate-shape units and is formed at temperatures below about 660 F (350 C). Also, a slender, needle-like (acicular) microstructure appearing in spring steel strip characterized by toughness and greater ductility than tempered Martensite. Bainite is a decomposition product of Austenite best developed at interrupted holding temperatures below those forming fine pearlite and above those giving Martensite.

AAC - Autoclaved Aerated Concrete

แปลว่า(Concrete Engineering) Exceptionally lightweight precast concrete with high thermal qualities and fire resistence. Suitable for cutting with ordinary hand tools. Mix design is composed of portland cement, sand or siliceous material, lime, gypsum, finely powdered aluminum, and water. Initial mix is a combination of portland cement, sand, lime and gypsum to produce a slurry. Finely powdered aluminum mixed into a paste is added prior to placement into large, rail-like forms. The finely powdered aluminum reacts with the alkaline components of the cement and lime to produce hydrogen gas, which increases the volume approximately five times producing a uniformly, dispersed cellular structure. Units are cut to required shape. Units are placed in an autoclave, an enclosed pressurized chamber, and steam cured at 3500 F. Approximately 80% of the ultimate volume consists of air voids.