Bainite

แปลว่า(english) A eutectoid transformation product of ferrite and a fine dispersion of carbide, generally formed at temperatures below 840 to 930 F (450 to 500 C): upper bainite is an aggregate containing parallel lath-shape units of ferrite, produces the so-called feathery appearance in optical microscopy, and is formed at temperatures above about 660 F (350 C); lower bainite consists of individual plate-shape units and is formed at temperatures below about 660 F (350 C). Also, a slender, needle-like (acicular) microstructure appearing in spring steel strip characterized by toughness and greater ductility than tempered Martensite. Bainite is a decomposition product of Austenite best developed at interrupted holding temperatures below those forming fine pearlite and above those giving Martensite.

Agglomerating Processes

แปลว่า(english) "Fine particles of limestone (flux) and iron ore are difficult to handle and transport because of dusting and decomposition, so the powdery material usually is processed into larger pieces. The raw material's properties determine the technique that is used by mills. 1) SINTER Baked particles that stick together in roughly one-inch chunks. Normally used for iron ore dust collected from the blast furnaces. 2) PELLETS Iron ore or limestone particles are rolled into little balls in a balling drum and hardened by heat. 3) BRIQUETTES Small lumps are formed by pressing material together. Hot Iron Briquetting (HBI) is a concentrated iron ore substitute for scrap for use in electric furnaces.

AAC - Autoclaved Aerated Concrete

แปลว่า(Concrete Engineering) Exceptionally lightweight precast concrete with high thermal qualities and fire resistence. Suitable for cutting with ordinary hand tools. Mix design is composed of portland cement, sand or siliceous material, lime, gypsum, finely powdered aluminum, and water. Initial mix is a combination of portland cement, sand, lime and gypsum to produce a slurry. Finely powdered aluminum mixed into a paste is added prior to placement into large, rail-like forms. The finely powdered aluminum reacts with the alkaline components of the cement and lime to produce hydrogen gas, which increases the volume approximately five times producing a uniformly, dispersed cellular structure. Units are cut to required shape. Units are placed in an autoclave, an enclosed pressurized chamber, and steam cured at 3500 F. Approximately 80% of the ultimate volume consists of air voids.