Batch Anneal

แปลว่า(english) The process by which a large, stationary stack of steel coils (4 coils high) is subjected to a long heat-treating cycle. This process enables the cold-rolled sheet to fully recrystallize into the softest possible product conforming to customer specifications. Controlling the recrystallization process makes a fine-grained microstructure easy to obtain, and minimizes the tendencies for retention of directional properties of the rolled steel which could produce undesirable shapes in the stamping of a cylindrical part such as a can. Also see Anneal and Continuous Anneal.

Brass

แปลว่า(english) An alloy that is 70% copper,30% zinc. One of the most widely used of the copper-zinc alloys; malleable and ductile; excellent cold-working but poor hot-working and machining properties; excellent for soft-soldering; good for silver alloy brazing or oxyacetylene welding, but fair for resistance or carbon-arc welding. Used for drawn cartridges, tubes, eyelets machine items and snap fasteners.

Beryllium Copper

แปลว่า(english) An alloy of copper and 2-3% beryllium with optionally fractional percentages of nickel or cobalt. Alloys of this series show remarkable age-hardening properties and an ultimate hardness of about 400 Brinell (Rockwell C43). Because of such hardness and good electrical conductivity, beryllium-copper is used in electrical switches, springs, etc.

Maximum Size Aggregate

แปลว่า(Concrete Engineering) Aggregate whose largest particle size is present in sufficient quantity to affect the physical properties of concrete; generally designated by the sieve size on which the maximum amount permitted to be retained is 5 or 10 percent by weight.

Bright Drawing

แปลว่า(english) The process of drawing hot rolled steel through a die to impart close dimensional tolerances, a bright scale free surface and improved mechanical properties. The product is termed bright steel.

index properties

แปลว่าดัชนีคุณสมบัติ (ดินหรือหิน)

Aging 2

แปลว่า(english) A change in properties that occurs at ambient or moderately elevated temperatures after hot working or a heat treating operation (quench aging in ferrous alloys), or after a cold working operation (strain aging). The change in properties is often, but not always, due to a phase change (precipitation), but does not involve a change in chemical composition. In a metal or alloy, a change in properties that generally occurs slowly at room temperature and more rapidly at higher temperatures.

Agglomerating Processes

แปลว่า(english) "Fine particles of limestone (flux) and iron ore are difficult to handle and transport because of dusting and decomposition, so the powdery material usually is processed into larger pieces. The raw material's properties determine the technique that is used by mills. 1) SINTER Baked particles that stick together in roughly one-inch chunks. Normally used for iron ore dust collected from the blast furnaces. 2) PELLETS Iron ore or limestone particles are rolled into little balls in a balling drum and hardened by heat. 3) BRIQUETTES Small lumps are formed by pressing material together. Hot Iron Briquetting (HBI) is a concentrated iron ore substitute for scrap for use in electric furnaces.

Baked Core

แปลว่า(english) A core which has been heated through sufficient time and temperature to produce the desired physical properties attainable from its oxidizing or thermal-setting binders.

acoustical properties

แปลว่ามีคุณสมบัติหลายอย่างในการป้องกันเสียงสะท้อน

Balanced Steel

แปลว่า(english) Steels in which the deoxidisation is controlled to produce an intermediate structure between a rimmed and killed steel, Sometimes referred to as semi-killed steels, they possess uniform properties throughout the ingot and amongst their applications are boiler plate and structural sections.

Age Hardening

แปลว่า(english) Hardening by aging, usually after rapid cooling or cold working. The term as applied to soft, or low carbon steels, relates to a wide variety of commercially important, slow, gradual changes that take place in properties of steels after the final treatment. These changes, which bring about a condition of increased hardness, elastic limit, and tensile strength with a consequent loss in ductility, occur during the period in which the steel is at normal temperatures.