 หรือคุณกำลังค้นหา Sulfate Resistance, aggregate

Maximum Size Aggregate

แปลว่า(Concrete Engineering) Aggregate whose largest particle size is present in sufficient quantity to affect the physical properties of concrete; generally designated by the sieve size on which the maximum amount permitted to be retained is 5 or 10 percent by weight.

lightweight aggregate

แปลว่ามวลรวมน้ำหนักเบา, มวลรวมเบา

Magnetite

แปลว่า(Concrete Engineering) An aggregate used in heavy weight concrete, consisting primarily of ferrous metaferrite (Fe304). A black magnetic iron ore with a specific gravity of approximately 5.2 and a Mohs hardness of about 6.

Absorbed Moisture

แปลว่า(Concrete Engineering) Moisture which is mechanically held in a material. In aggregates, that water which is not available to become part of the mixing water is designated "absorbed" water.

Unit Water Content

แปลว่า(Concrete Engineering) The quantity of water per unit volume of freshly mixed concrete, often expressed as gallons or pounds per cubic yard. This is the quantity of water on which the water cement ratio is based, and does not include water absorbed by the aggregate

angular aggregate

แปลว่ามวลรวมก้อนเหลี่ยม

flaky aggregate

แปลว่ามวลรวมรูปร่างแบน

Alkali-Aggregate Reaction

แปลว่า(Concrete Engineering) Older terminology for Alkali-Silica Reactivity (ASR).

gap-graded aggregate

แปลว่ามวลรวมข้ามขนาด

Sand (ASTM C125)

แปลว่า(Concrete Engineering) That portion of an aggregate passing the No. 4 (4.76 mm) sieve and predominantly retained on the No. 200 (74 micron) sieve.

coarse aggregate

แปลว่ามวลรวมหยาบ

Bainite

แปลว่า(english) A eutectoid transformation product of ferrite and a fine dispersion of carbide, generally formed at temperatures below 840 to 930 F (450 to 500 C): upper bainite is an aggregate containing parallel lath-shape units of ferrite, produces the so-called feathery appearance in optical microscopy, and is formed at temperatures above about 660 F (350 C); lower bainite consists of individual plate-shape units and is formed at temperatures below about 660 F (350 C). Also, a slender, needle-like (acicular) microstructure appearing in spring steel strip characterized by toughness and greater ductility than tempered Martensite. Bainite is a decomposition product of Austenite best developed at interrupted holding temperatures below those forming fine pearlite and above those giving Martensite.