Breakout

แปลว่า(english) An accident caused by the failure of the walls of the hearth of the furnace resulting in liquid iron or slag (or both) flowing uncontrolled out of the blast furnace.

Basic Oxygen Process

แปลว่า(english) (BOP) A process in which molten steel is produced in a furnace by blowing oxygen into molten iron, scrap and flux materials. The furnace is known as Basic Oxygen Furnace (BOF).

Magnetite

แปลว่า(Concrete Engineering) An aggregate used in heavy weight concrete, consisting primarily of ferrous metaferrite (Fe304). A black magnetic iron ore with a specific gravity of approximately 5.2 and a Mohs hardness of about 6.

Acid-Process

แปลว่า(english) A process of making steel, either Bessemer, open-hearth or electric, in which the furnace is lined with a siliceous refractory and for which low phosphorus pig iron is required as this element is not removed.

Bending Angle

แปลว่า(english) A 'V-shaped' piece of angle iron attached to the rear of the coil car in the Strip Steel, which is used to help the operator put bends into the front end of a coil.

Acid Process 1

แปลว่า(english) A process of making steel, either Bessemer, open-hearth or electric, in which the furnace is lined with a siliceous refractory and for which low phosphorus pig iron is required as this element is not removed.

Basic Oxygen Process 2

แปลว่า(english) A steel making process wherein oxygen of the highest purity is blown onto the surface of a bath of molten iron contained in a basic lined and ladle shaped vessel. The melting cycle duration is extremely short with quality comparable to Open Hearth Steel.

Burr

แปลว่า(english) The very subtle ridge on the edge of strip steel left by cutting operations such as slitting, trimming, shearing, or blanking. For example, as a steel processor trims the sides of the sheet steel parallel or cuts a sheet of steel into strips, its edges will bend with the direction of the cut.

planc

แปลว่าพื้นราบ, ราบ, ระดับ, ปราบให้เรียบ, ทำให้แนวราบ, เครื่องปาดดิน หรือทราย หรือปูน, กบใสไม้, กบไสโลหะ iron plane กบไสโลหะ long plane กบบรรทัด moulding plane กบไสคิ้ว, กบร่อง rabbet plane กบถากไม้ smoothing plane กบแต่งผิว, กบปาด wooden plane กบไสไม้

Blast Furnace Slag

แปลว่า(Concrete Engineering) A non-metallic waste product developed in the manufacture of pig iron, consisting basically of a mixture of lime, silica and alumina, the same oxides that make up portland cement, but not in the same proportions or forms. It is used both in the manufacture of portland blast furnace slag cement and as an aggregate for lightweight concrete.

Billet 2

แปลว่า(english) A solid semi-finished round or square product that has been hot worked by forging, rolling, or extrusion. An iron or steel billet has a minimum width or thickness of 1 1/2 in. and the cross-sectional area varies from 2 1/4 to 36 sq. in. For nonferrous metals, it may also be a casting suitable for finished or semi-finished rolling or for extrusion.

AAC - Autoclaved Aerated Concrete

แปลว่า(Concrete Engineering) Exceptionally lightweight precast concrete with high thermal qualities and fire resistence. Suitable for cutting with ordinary hand tools. Mix design is composed of portland cement, sand or siliceous material, lime, gypsum, finely powdered aluminum, and water. Initial mix is a combination of portland cement, sand, lime and gypsum to produce a slurry. Finely powdered aluminum mixed into a paste is added prior to placement into large, rail-like forms. The finely powdered aluminum reacts with the alkaline components of the cement and lime to produce hydrogen gas, which increases the volume approximately five times producing a uniformly, dispersed cellular structure. Units are cut to required shape. Units are placed in an autoclave, an enclosed pressurized chamber, and steam cured at 3500 F. Approximately 80% of the ultimate volume consists of air voids.