Burning

แปลว่า(english) (1) Permanently damaging a metal or alloy by heating to cause either incipient melting or intergranular oxidation. (2) In grinding getting the work hot enough to cause discoloration or to change the microstructure by tempering or hardening.

Bloom 2

แปลว่า(english) A semi-finished hot rolled product, rectangular in cross section, produced on a blooming mill. For iron and steel, the width is not more than twice the thickness, and the cross-sectional area is usually not less than 36 sq. in. Iron and steel blooms are sometimes made by forging.

Bainite

แปลว่า(english) A eutectoid transformation product of ferrite and a fine dispersion of carbide, generally formed at temperatures below 840 to 930 F (450 to 500 C): upper bainite is an aggregate containing parallel lath-shape units of ferrite, produces the so-called feathery appearance in optical microscopy, and is formed at temperatures above about 660 F (350 C); lower bainite consists of individual plate-shape units and is formed at temperatures below about 660 F (350 C). Also, a slender, needle-like (acicular) microstructure appearing in spring steel strip characterized by toughness and greater ductility than tempered Martensite. Bainite is a decomposition product of Austenite best developed at interrupted holding temperatures below those forming fine pearlite and above those giving Martensite.

Cellular Concrete

แปลว่า(Concrete Engineering) A lightweight product consisting of portland cement, cement-pozzolan, cement sand, lime-pozzolan, or lime-sand pastes, or pastes containing blends of these ingredients and having a homogenous void or cell structure, attained with gas forming chemicals or foaming agents. For cellular concretes, containing binder ingredients other than or in addition to portland cement, autoclave curing is usually employed.

Blast Furnace Slag

แปลว่า(Concrete Engineering) A non-metallic waste product developed in the manufacture of pig iron, consisting basically of a mixture of lime, silica and alumina, the same oxides that make up portland cement, but not in the same proportions or forms. It is used both in the manufacture of portland blast furnace slag cement and as an aggregate for lightweight concrete.

Billet 2

แปลว่า(english) A solid semi-finished round or square product that has been hot worked by forging, rolling, or extrusion. An iron or steel billet has a minimum width or thickness of 1 1/2 in. and the cross-sectional area varies from 2 1/4 to 36 sq. in. For nonferrous metals, it may also be a casting suitable for finished or semi-finished rolling or for extrusion.

Blasting (Blast Cleaning)

แปลว่า(english) A process for cleaning or finishing metal objects by use of an air blast or centrifugal wheel that throws abrasive particles against the surface of the work pieces. Small, irregular particles of steel or iron are used as the abrasive in grit blasting, and steel or iron balls in shot blasting.

Batch Anneal

แปลว่า(english) The process by which a large, stationary stack of steel coils (4 coils high) is subjected to a long heat-treating cycle. This process enables the cold-rolled sheet to fully recrystallize into the softest possible product conforming to customer specifications. Controlling the recrystallization process makes a fine-grained microstructure easy to obtain, and minimizes the tendencies for retention of directional properties of the rolled steel which could produce undesirable shapes in the stamping of a cylindrical part such as a can. Also see Anneal and Continuous Anneal.

Brazing

แปลว่า(english) Joining metals by fusion of nonferrous alloys that have melting points above 800 F (425C), but lower than those of the metals being joined. May be accomplished by a torch. Filler metal is ordinarily in rod form in torch brazing; whereas in furnace and dip brazing the work material is first assembled and the filler metal may then be applied as wire, washers, clips, bands, or may be bonded, as in brazing sheet.

Bend Test

แปลว่า(english) Various tests which is used to ascertain the toughness and ductility of a metal product, in which the material is bent around its axis and/ or around an outside radius. A complete test might specify such a bend to be both with and against the direction of grain. For testing, samples should be edge filed to remove burrs and any edgewise cracks resulting from slitting or shearing. If a vice is to be employed, then you must line the jaws with some soft metal, to permit a flow of the metal in the piece being tested.