ผลการค้นหา

Bismuth

แปลว่า(english) Chemical symbol Bi. A soft, course cystalline heavy metal with a silvery white color and pinkish tinge; usually produced as a by-product of copper,leaad and other metals. Has a thermal conductivity lower than all other metals except mercury. Used as alloying agent but leading use is in pharmaceuticals.

Box Annealing 2

แปลว่า(english) A process of annealing a ferrous alloy in a closed metal container, with or without packing materials, in order to minimize the effects of oxidation. The charge is normally heated slowly to a temperature below the transformation range, but occasionally above or within it, and then is slowly cooled.

Pozzolan (ASTM C 618)

แปลว่า(Concrete Engineering) A siliceous, or siliceous and aluminous material, which in itself possesses little or no cementitious value but will, in a finely divided form, such as a powder or liquid and in the presence of moisture, chemically react with calcium hydroxide at ordinary temperatures to form permanent, insoluble compounds possessing cementitious properties.

Burr

แปลว่า(english) The very subtle ridge on the edge of strip steel left by cutting operations such as slitting, trimming, shearing, or blanking. For example, as a steel processor trims the sides of the sheet steel parallel or cuts a sheet of steel into strips, its edges will bend with the direction of the cut.

Blast Furnace

แปลว่า(english) 1) A furnace in which solid fuel (limestone, coke, iron ore) is combined with high-pressure, hot air blast (120,000 psi) to smelt ore in a continuous process (They are never stopped. They can be slowed down or idled). A Blast Furnace in the iron and steel industry is used to produce liquid iron.

Cellular Concrete

แปลว่า(Concrete Engineering) A lightweight product consisting of portland cement, cement-pozzolan, cement sand, lime-pozzolan, or lime-sand pastes, or pastes containing blends of these ingredients and having a homogenous void or cell structure, attained with gas forming chemicals or foaming agents. For cellular concretes, containing binder ingredients other than or in addition to portland cement, autoclave curing is usually employed.

Construction Joint

แปลว่า(Concrete Engineering) The contact between the placed concrete and concrete surfaces, against or upon which concrete is to be placed and to which new concrete is to adhere, that has become so rigid that the new concrete cannot be incorporated integrally by vibration with that previously placed. Unformed construction joints are horizontally placed or nearly so.

Moment of inertia (I):

แปลว่า(english) Moment of inertia has two distinct but related meanings: 1) it is a property of a an object relating to the magnitude of the moment required to rotate the object and overcome its inertia. 2) A property of a two dimensional cross section shape with respect to an axis, usually an axis through the centroid of the shape.

Break Test (for tempered steel)

แปลว่า(english) A method of testing hardened and tempered high carbon spring steel strip wherein the specimen is held and bent across the grain in a vice-like calibrated testing machine. Pressure is applied until the metal fractures at which point a reading is taken and compared with a standard chart of brake limitations for various thickness ranges.

Boron (chemical symbol B)

แปลว่า(english) Element N. 5 of the periodic system. Atomic weight 10.82. It is gray in color, ignites at about 1112 (degrees) F. and burns with a brilliant green flame, but its melting point in a non-oxidizing atmosphere is about 4000 (degrees) F. Boron is used in steel in minute quantities for one purpose only- to increase the hardenability as in case hardening and to increase strength and hardness penetration.

Basic Oxygen Furnace (BOF)

แปลว่า(english) "WHAT A pear-shaped furnace, lined with refractory bricks, that refines molten iron from the blast furnace and scrap into steel. Up to 30% of the charge into the BOF can be scrap, with hot metal accounting for the rest. WHY BOFs, which can refine a heat (batch) of steel in less than 45 minutes, replaced open-hearth furnaces in the 1950s; the latter required five to six hours to process the metal. The BOF's rapid operation, lower cost and ease of control give it a distinct advantage over previous methods. HOW Scrap is dumped into the furnace vessel, followed by the hot metal from the blast furnace. A lance is lowered from above, through which blows a high-pressure stream of oxygen to cause chemical reactions that separate impurities as fumes or slag. Once refined, the liquid steel and slag are poured into separate containers. "

Age Hardening

แปลว่า(english) Hardening by aging, usually after rapid cooling or cold working. The term as applied to soft, or low carbon steels, relates to a wide variety of commercially important, slow, gradual changes that take place in properties of steels after the final treatment. These changes, which bring about a condition of increased hardness, elastic limit, and tensile strength with a consequent loss in ductility, occur during the period in which the steel is at normal temperatures.