pressure ratio switch
แปลว่าสวิทช์ของเครื่องควบคุมอัตรากำลังดันของเครื่องอัดแกส
Brinell Hardness Testing
แปลว่า(english) Method of determining the hardness of materials; involves impressing a hardened ball of specified diameter into the material surface at a known pressure (10-mm ball, 500-kg load for aluminum alloys). The Brinell hardness number results from calculations involving the load and the spherical area of the ball impression. Direct-reading testing are generally used for routine inspection of forgings, and as a heat treat control function.
earth pressure cell
แปลว่าเครื่องมือที่ใช้วัดแรงดันดินในทิศทางต่าง ๆ ที่ติดตั้งไว้ในตัวเขื่อนดิน
Z-Mill
แปลว่า(english) The full name for z-mill is Sendzimir mill. A Z-mill operates with a very small diameter work roll, normally about 2 inches, backed up by a number of rolls in a pyramid-shaped stack. This roll set up allows you to exert extremely high forces through the work roll and yet keep the work roll from extreme flexing. The take-up roll on the Z-Mill also exerts a tension on the coil as it comes through the mill. The combination of high pressure and tension makes the mill capable of rolling material thin and flat.
excessive pore water pressure
แปลว่าค่าเปลี่ยนแปลงความดันน้ำในดิน
Brinell Hardness Test
แปลว่า(english) A common standard method of measuring the hardness of materials. The smooth surface of the metal is subjected to indentation by a hardened steel ball under pressure. The diameter of the indentation, in the material surface, is then measured by a microscope and the hardness value is read from a chart or determined by a prescribed formula.
pressure system for fuel supply
แปลว่าระบบบังคับการจ่ายน้ำมันเชื้อเพลิงในเครื่องยนต์
high-pressure
แปลว่าความกดหรือแรงอัดสูง
non-pressure welding
แปลว่าการเชื่อมโลหะที่ไม่ใช้แรงอัดใด ๆ
Basic Oxygen Furnace (BOF)
แปลว่า(english) "WHAT A pear-shaped furnace, lined with refractory bricks, that refines molten iron from the blast furnace and scrap into steel. Up to 30% of the charge into the BOF can be scrap, with hot metal accounting for the rest. WHY BOFs, which can refine a heat (batch) of steel in less than 45 minutes, replaced open-hearth furnaces in the 1950s; the latter required five to six hours to process the metal. The BOF's rapid operation, lower cost and ease of control give it a distinct advantage over previous methods. HOW Scrap is dumped into the furnace vessel, followed by the hot metal from the blast furnace. A lance is lowered from above, through which blows a high-pressure stream of oxygen to cause chemical reactions that separate impurities as fumes or slag. Once refined, the liquid steel and slag are poured into separate containers. "
Water Vapor Pressure
แปลว่า(Concrete Engineering) The pressure exerted by water vapor. Air that contains higher amounts of water vapor exerts a higher vapor pressure than air which has a lower amount of has a higher water vapor pressure In concrete water vapor pressure is calculated by the difference between the vapor pressure of the concrete and the ambient relative humidity and temperature and in contact with the soil. that is calculated by; based upon relative humidity and temperature. The greater the difference between the water vapor and ambient humidity and temperature, in degrees Fahrenheit. the greater the water vapor pressure exerted.
Preplaced Concrete
แปลว่า(Concrete Engineering) Concrete manufactured by placing clean, graded coarse aggregate in a form and later injecting a portland cement-sand grout under pressure, to fill the voids.