Accordion Reed Steel

แปลว่า(english) Hardened, tempered, polished and blued or yellow flat steel with dressed edges. Carbon content about 1.00. Material has to possess good flatness, uniform hardness and high elasticity.

Kelly Ball

แปลว่า(Concrete Engineering) A device for determining the consistency of fresh concrete. It is sometimes used as an alternative to the slump test.

Moist Room

แปลว่า(Concrete Engineering) A room used for storing and curing cementitious test specimens. The atmosphere of this room is maintained at a temperature of 73.4 3.0'F or 23.0*1.7'0 and relative humidity of at least 98 percent. These facilities must be adequate to continually maintain free moisture on the exteriors of test specimens.

Magnetite

แปลว่า(Concrete Engineering) An aggregate used in heavy weight concrete, consisting primarily of ferrous metaferrite (Fe304). A black magnetic iron ore with a specific gravity of approximately 5.2 and a Mohs hardness of about 6.

Slump Cone

แปลว่า(Concrete Engineering) A metal mold in the form of a truncated cone with a top diameter of 4”, a bottom diameter of 8”, and a height of 12”, used to fabricate the specimen for a slump test.

Black Oil Tempered Spring Steel Strip (Scaleless Blue)

แปลว่า(english) A flat cold rolled usually .70/.80 medium high carbon steel strip, blue-black in color, which has been quenched in oil and drawn to desired hardness. While it looks and acts much like blue tempered spring steel and carries a Rockwell hardness of C44/47, it has not been polished and is lower in carbon content. Used for less exacting requirements than clock spring steel, such as snaps, lock springs, hold down springs, trap springs, etc. It will take a more severe bend before fracture than will clock spring, but it does not have the same degree of spring-back.

Aging 1

แปลว่า(english) A change in the properties of certain metal and alloys (such as steel) that occurs at ambient or moderately elevated temperatures after a hot working heat treatment or cold working operation. Typical properties impacted are hardness, yield strength, tensile strength, ductility, impact value, formability, magnetic properties, etc. See also Non-aging.

Software engineering

แปลว่า(Software Engineering) a discipline that encompasses the process associated with software development, the methods used to analyze, design and test computer software, the management techniques associated with the control and monitoring of software projects and the tools used to support process, methods, and techniques.

Ottawa Sand

แปลว่า(Concrete Engineering) A sand used as a standard in testing hydraulic cements by means of mortar test specimens. Sand is produced by processing silica rock particles obtained by hydraulic mining of the orthoquartzite situated in open-pit deposits near Ottawa, Illinois; naturally rounded grains of nearly pure quartz.

Toxicity

แปลว่า(Environmental Engineering) A U.S. EPA hazardous waste characteristic defined with a rigorous test procedure, the TCLP (for Toxicity Characteristic Leaching Procedure). In the procedure, a waste is extracted for 24 hours with an acetic acid solution. The acid extract is then analyzed for the presence of any of the contaminants listed in the procedure.

Boron (chemical symbol B)

แปลว่า(english) Element N. 5 of the periodic system. Atomic weight 10.82. It is gray in color, ignites at about 1112 (degrees) F. and burns with a brilliant green flame, but its melting point in a non-oxidizing atmosphere is about 4000 (degrees) F. Boron is used in steel in minute quantities for one purpose only- to increase the hardenability as in case hardening and to increase strength and hardness penetration.

Age Hardening

แปลว่า(english) Hardening by aging, usually after rapid cooling or cold working. The term as applied to soft, or low carbon steels, relates to a wide variety of commercially important, slow, gradual changes that take place in properties of steels after the final treatment. These changes, which bring about a condition of increased hardness, elastic limit, and tensile strength with a consequent loss in ductility, occur during the period in which the steel is at normal temperatures.