Basic Oxygen Process

แปลว่า(english) (BOP) A process in which molten steel is produced in a furnace by blowing oxygen into molten iron, scrap and flux materials. The furnace is known as Basic Oxygen Furnace (BOF).

Rod (tamping) (ASTM C24l)

แปลว่า(Concrete Engineering) A round, straight steel rod, 5/8' in diameter and approximately 24' in length, having the tamping end rounded into a hemispherical tip, the diameter of which is 5/8'.

Tilt-up

แปลว่า(Concrete Engineering) A method of concrete construction such as where members are cast horizontally near their eventual position, usually on a recently placed slab, and then tilted into place after removal of forms.

Secured landfill

แปลว่า(Environmental Engineering) A landfill which has containment measures such as liners and a leachate collection system so that materials placed in the landfill will not migrate into the surrounding soil, air and water.

Change of State

แปลว่า(Concrete Engineering) The process whereby liquid is heated to the point of evaporation changing the liquid into a gas the condensation of a gas on a cooler surface returning it from gaseous to liquid form.

Bending Angle

แปลว่า(english) A 'V-shaped' piece of angle iron attached to the rear of the coil car in the Strip Steel, which is used to help the operator put bends into the front end of a coil.

Basic Oxygen Furnace (BOF)

แปลว่า(english) "WHAT A pear-shaped furnace, lined with refractory bricks, that refines molten iron from the blast furnace and scrap into steel. Up to 30% of the charge into the BOF can be scrap, with hot metal accounting for the rest. WHY BOFs, which can refine a heat (batch) of steel in less than 45 minutes, replaced open-hearth furnaces in the 1950s; the latter required five to six hours to process the metal. The BOF's rapid operation, lower cost and ease of control give it a distinct advantage over previous methods. HOW Scrap is dumped into the furnace vessel, followed by the hot metal from the blast furnace. A lance is lowered from above, through which blows a high-pressure stream of oxygen to cause chemical reactions that separate impurities as fumes or slag. Once refined, the liquid steel and slag are poured into separate containers. "

Bottle Top Mold

แปลว่า(english) Ingot mold, with the top constricted; used in the manufacture of capped steel, the metal in the constriction being covered with a cap fitting into the bottle-neck, which stops rimming action by trapping escaping gases.

AAC - Autoclaved Aerated Concrete

แปลว่า(Concrete Engineering) Exceptionally lightweight precast concrete with high thermal qualities and fire resistence. Suitable for cutting with ordinary hand tools. Mix design is composed of portland cement, sand or siliceous material, lime, gypsum, finely powdered aluminum, and water. Initial mix is a combination of portland cement, sand, lime and gypsum to produce a slurry. Finely powdered aluminum mixed into a paste is added prior to placement into large, rail-like forms. The finely powdered aluminum reacts with the alkaline components of the cement and lime to produce hydrogen gas, which increases the volume approximately five times producing a uniformly, dispersed cellular structure. Units are cut to required shape. Units are placed in an autoclave, an enclosed pressurized chamber, and steam cured at 3500 F. Approximately 80% of the ultimate volume consists of air voids.

Cement, Portland (ASTM C150) (Concrete Engineering)

แปลว่าA powdery substance made by burning, at a high temperature, a mixture of clay and limestone producing lumps called “clinkers” which are ground into a fine powder consisting of hydraulic calcium silicates. For non-portland cements, see aluminous cement.

Dry Rodded Weight

แปลว่า(Concrete Engineering) The weight of dry aggregate rodded into a cylindrical container of diameter approximately equal to the height, each of 3 layers rodded 25 times, and the excess aggregate struck off level with the top of the container

Brinell Hardness

แปลว่า(english) The hardness of a metal or part, as represented by the number obtained from the ratio between the load applied on the spherical area of the impression made by a steel ball forced into the surface of the material tested.