Bainite

แปลว่า(english) A eutectoid transformation product of ferrite and a fine dispersion of carbide, generally formed at temperatures below 840 to 930 F (450 to 500 C): upper bainite is an aggregate containing parallel lath-shape units of ferrite, produces the so-called feathery appearance in optical microscopy, and is formed at temperatures above about 660 F (350 C); lower bainite consists of individual plate-shape units and is formed at temperatures below about 660 F (350 C). Also, a slender, needle-like (acicular) microstructure appearing in spring steel strip characterized by toughness and greater ductility than tempered Martensite. Bainite is a decomposition product of Austenite best developed at interrupted holding temperatures below those forming fine pearlite and above those giving Martensite.

Nitrogen fixation

แปลว่า(Environmental Engineering) The conversion of atmospheric (or dissolved) nitrogen gas into nitrate by microorganisms.

Bottle Top Mold

แปลว่า(english) Ingot mold, with the top constricted; used in the manufacture of capped steel, the metal in the constriction being covered with a cap fitting into the bottle-neck, which stops rimming action by trapping escaping gases.

Blast Cleaning (blasting)

แปลว่า(english) A process for cleaning or finishing metal objects by use of an air jet or centrifugal wheel that propels abrasive particles (grit, sand, or shot) against the surfaces of the workpiece at high velocity.

Black Plate

แปลว่า(english) A light weight or a thin uncoated steel sheet or strip so called because of its dark oxide coloring prior to pickling. It is manufactured by two different processes. (1) Form sheet bar on single stand sheet mills or sheet mills in tandem. This method is now almost obsolete. (2) On modern, high speed continuous tandem cold reduction mills from coiled hot rolled pickled wide strip into ribbon wound coils to finished gage. Sizes range from 12 to 32 in width, and in thicknesses from 55 lbs. to 275 lbs. base box weight. It is used either as is for stampings, or may be enameled or painted or tin or terne coated.

Blister Steel

แปลว่า(english) High-carbon steel produced by carburizing wrought iron. The bar, originally smooth, is covered with small blisters when removed from the cementation (carburizing) furnace.

Beta testing

แปลว่า(Software Engineering) testing that is conducted by the user

Blowhole 2

แปลว่า(english) A cavity which was produced during the solidification of metal by evolved gas, which in failing to escape is held in pockets.

Carbonation

แปลว่า(Concrete Engineering) 1) Reaction between the products of portland cement (soluble calcium hydroxides), water and carbon dioxide to produce insoluble calcium carbonate (efflorescence). 2) Soft white, chalky surface dusting of freshly placed, unhardened concrete caused by carbon dioxide from unvented heaters or gasoline powered equipment in an enclosed space. 3) Carbonated, dense, impermeable to absorption, top layer of the surface of concrete caused by surface reaction to carbon dioxide. This carbonated layer becomes denser and deeper over a period of time. 4) Reaction with carbon dioxide which produces a slight shrinkage in concrete. Improves chemical stability. Concrete masonry units during manufacturing may be deliberately exposed to carbon dioxide after reaching 80% strength to induce carbonation shrinkage to make the units more dimensionally stable. Future drying shrinkage is reduced by as much as 30%.

Brinell Hardness Test

แปลว่า(english) A common standard method of measuring the hardness of materials. The smooth surface of the metal is subjected to indentation by a hardened steel ball under pressure. The diameter of the indentation, in the material surface, is then measured by a microscope and the hardness value is read from a chart or determined by a prescribed formula.