cold water pipe

แปลว่าท่อน้ำเย็น

Brown Sharp Gages

แปลว่า(english) A standard series of sizes refered to by numbers, in which the diameter of wire or thickness of sheet metal is generally produced and which is used in the manufacture of brass, bronze, copper, copper-base alloys and aluminum. These gage numbers have a definite relationship to each other. In this system, the decimal thickness is reduced by 50% every six gage numbers- while temper is expressed by the number of B&S gage numbers as cold reduced in thickness from previous annealing. For each B&S gage number in thickness reduction, where is assigned a hardness value of 1/4 hard.

cold drawn steel wire

แปลว่าลวดเหล็กดึงเย็น

flat-cold chisel

แปลว่าเหล็กสกัดปากแบน มีด้ามเป็นเหล็กใช้สกัดเหล็กที่ยื่น

Age Hardening

แปลว่า(english) Hardening by aging, usually after rapid cooling or cold working. The term as applied to soft, or low carbon steels, relates to a wide variety of commercially important, slow, gradual changes that take place in properties of steels after the final treatment. These changes, which bring about a condition of increased hardness, elastic limit, and tensile strength with a consequent loss in ductility, occur during the period in which the steel is at normal temperatures.

Bridling

แปลว่า(english) The cold working of dead soft annealed strip metal immediately prior to a forming, bending, or drawing operation. A process designed to prevent the formulation of Luder's lines. Caution-Bridled metal should be used promptly and not permitted to (of itself) return to its pre-bridled condition.

Band Saw Steel (Wood)

แปลว่า(english) A hardened tempered bright polished high carbon cold rolled spring steel strip produced especially for use in the manufacture of band saws for sawing wood, non ferrous metals, and plastics. Usually carries some nickel and with a Rockwell value of approximately C40/45.

Aging 2

แปลว่า(english) A change in properties that occurs at ambient or moderately elevated temperatures after hot working or a heat treating operation (quench aging in ferrous alloys), or after a cold working operation (strain aging). The change in properties is often, but not always, due to a phase change (precipitation), but does not involve a change in chemical composition. In a metal or alloy, a change in properties that generally occurs slowly at room temperature and more rapidly at higher temperatures.

Brasses

แปลว่า(english) Copper base alloys in which zinc is the principal alloying element. Brass is harder and mechanically stronger than either of its alloying elements copper or zinc. It is formable and ductile; develops high tensile strength with cold-working and is not heat treatable.

flat cold chisel

แปลว่าเหล็กสะกัดปากแบนสำหรับใช้ตัดแผ่นโลหะ

Black Plate

แปลว่า(english) A light weight or a thin uncoated steel sheet or strip so called because of its dark oxide coloring prior to pickling. It is manufactured by two different processes. (1) Form sheet bar on single stand sheet mills or sheet mills in tandem. This method is now almost obsolete. (2) On modern, high speed continuous tandem cold reduction mills from coiled hot rolled pickled wide strip into ribbon wound coils to finished gage. Sizes range from 12 to 32 in width, and in thicknesses from 55 lbs. to 275 lbs. base box weight. It is used either as is for stampings, or may be enameled or painted or tin or terne coated.

Batch Anneal

แปลว่า(english) The process by which a large, stationary stack of steel coils (4 coils high) is subjected to a long heat-treating cycle. This process enables the cold-rolled sheet to fully recrystallize into the softest possible product conforming to customer specifications. Controlling the recrystallization process makes a fine-grained microstructure easy to obtain, and minimizes the tendencies for retention of directional properties of the rolled steel which could produce undesirable shapes in the stamping of a cylindrical part such as a can. Also see Anneal and Continuous Anneal.