ผลการค้นหา

Blister

แปลว่า(english) 1) Coating defect consisting of the formation of bubbles in a coating, which appear as hemispherical elevations. The blisters are hollow, and are usually caused by entrapped air or solvent. 2) A raised spot on the surface on the surface of metal due to expansion of gas which causes a subsurface metal separation such as inclusions and small laminations.

Bainite

แปลว่า(english) A eutectoid transformation product of ferrite and a fine dispersion of carbide, generally formed at temperatures below 840 to 930 F (450 to 500 C): upper bainite is an aggregate containing parallel lath-shape units of ferrite, produces the so-called feathery appearance in optical microscopy, and is formed at temperatures above about 660 F (350 C); lower bainite consists of individual plate-shape units and is formed at temperatures below about 660 F (350 C). Also, a slender, needle-like (acicular) microstructure appearing in spring steel strip characterized by toughness and greater ductility than tempered Martensite. Bainite is a decomposition product of Austenite best developed at interrupted holding temperatures below those forming fine pearlite and above those giving Martensite.

Pumping (of Pavements)

แปลว่า(Concrete Engineering) The ejection of a mixture of water and solid materials such as clay or silt along cracks, transverse or longitudinal joints, and along pavement edges caused by downward slab movement due to the passage of heavy loads, machinery or equipment over the pavement after free water has accumulated in or on the subbase, subgrade or basecourse.

Batch Anneal

แปลว่า(english) The process by which a large, stationary stack of steel coils (4 coils high) is subjected to a long heat-treating cycle. This process enables the cold-rolled sheet to fully recrystallize into the softest possible product conforming to customer specifications. Controlling the recrystallization process makes a fine-grained microstructure easy to obtain, and minimizes the tendencies for retention of directional properties of the rolled steel which could produce undesirable shapes in the stamping of a cylindrical part such as a can. Also see Anneal and Continuous Anneal.

Elastic energy:

แปลว่า(english) The energy stored in deformed elastic material (e.g., a watch spring). Elastic energy equals where k is the stiffness, and is the associated deflection. Elastic energy is sometimes called elastic potential energy because it can be recovered when the object returns to its original shape; see potential energy.

Potential Energy:

แปลว่า(english) The energy stored in a raised object (e.g. the weights in a grandfather clock). Potential energy equals mgh, where m is mass, g is the acceleration of gravity, and h is the vertical distance from a reference location. It is called potential energy because the energy can be regained when the object is lowered. This type of potential energy is sometimes called gravitational potential energy in order to distinguish it from elastic potential energy: see elastic energy.

Dry Rodded Weight

แปลว่า(Concrete Engineering) The weight of dry aggregate rodded into a cylindrical container of diameter approximately equal to the height, each of 3 layers rodded 25 times, and the excess aggregate struck off level with the top of the container

Wetland

แปลว่า(Environmental Engineering) Semi-aquatic land, that is land that is either inundated or saturated by water for varying periods of time during each year, and that supports aquatic vegetation which is specifically adapted for saturated soil conditions.

Stiffness:

แปลว่า(english) This is a general term which may be applied to materials or structures. When a force is applied to a structure, there is a displacement in the direction of the force; stiffness is the ratio of the force divided by the displacement. High stiffness means that a large force produces a small displacement. When discussing the stiffness of a material, the concept is the same, except that stress substitutes for force, and strain substitutes for displacement; see modulus of elasticity.

AAC - Autoclaved Aerated Concrete

แปลว่า(Concrete Engineering) Exceptionally lightweight precast concrete with high thermal qualities and fire resistence. Suitable for cutting with ordinary hand tools. Mix design is composed of portland cement, sand or siliceous material, lime, gypsum, finely powdered aluminum, and water. Initial mix is a combination of portland cement, sand, lime and gypsum to produce a slurry. Finely powdered aluminum mixed into a paste is added prior to placement into large, rail-like forms. The finely powdered aluminum reacts with the alkaline components of the cement and lime to produce hydrogen gas, which increases the volume approximately five times producing a uniformly, dispersed cellular structure. Units are cut to required shape. Units are placed in an autoclave, an enclosed pressurized chamber, and steam cured at 3500 F. Approximately 80% of the ultimate volume consists of air voids.

Abrasive 2

แปลว่า(english) Natural – sandstone,emery,corundum,diamonds, or Artificial – silicon carbide,aluminum oxide – material used for making grinding wheels,andpaper,abrasive and lapping compunds.

Back Rake

แปลว่า(english) The angular surface ground back from the cutting edge of cutting tools. On lathe cutting tools. The rake is positive if the face slopws down from the cutting edge toward the shank, and negative if the face sloopes upward toward the shank.