Addition Agent

แปลว่า(english) 1) Any material added to a charge of molten metal in bath or ladle to bring alloy to specifications, 2) reagent added to plating bath.

Box Annealing

แปลว่า(english) Annealing a metal or alloy in a sealed container under conditions that minimize oxidation. In box annealing a ferrous alloy, the charge is usually heated slowly to a temperature below the transformation range, but sometimes above or within it, and is then cooled slowly; this process is also called close annealing or pot annealing.

Brass

แปลว่า(english) An alloy that is 70% copper,30% zinc. One of the most widely used of the copper-zinc alloys; malleable and ductile; excellent cold-working but poor hot-working and machining properties; excellent for soft-soldering; good for silver alloy brazing or oxyacetylene welding, but fair for resistance or carbon-arc welding. Used for drawn cartridges, tubes, eyelets machine items and snap fasteners.

Bronze 2

แปลว่า(english) Primarily an alloy of copper and tin, but additionally, the name is used when referring to other alloys not containing tin, for example, aluminum bronze, manganese bronze, and beryllium bronze.

Burn

แปลว่า(english) 1) Process of cutting metal by a stream of fuel and oxygen, 2) to permanently damage a metal or alloy by heating to cause either incipient melting or intergranular oxidation.

Bronze

แปลว่า(english) An alloy containing 90% copper and 10% tin. Used for screws, wire, hardware, wear plates, bushings and springs; it is somewhat stronger than copper and brass and has equal or better ductility.

Base Metal

แปลว่า(english) (1) The metal present in the largest proportion in an alloy; (2) the metal to be brazed, cut or welded; (3) after welding the part of the metal that was not melted during the process.

Burning

แปลว่า(english) (1) Permanently damaging a metal or alloy by heating to cause either incipient melting or intergranular oxidation. (2) In grinding getting the work hot enough to cause discoloration or to change the microstructure by tempering or hardening.

Beryllium Copper

แปลว่า(english) An alloy of copper and 2-3% beryllium with optionally fractional percentages of nickel or cobalt. Alloys of this series show remarkable age-hardening properties and an ultimate hardness of about 400 Brinell (Rockwell C43). Because of such hardness and good electrical conductivity, beryllium-copper is used in electrical switches, springs, etc.

Box Annealing 2

แปลว่า(english) A process of annealing a ferrous alloy in a closed metal container, with or without packing materials, in order to minimize the effects of oxidation. The charge is normally heated slowly to a temperature below the transformation range, but occasionally above or within it, and then is slowly cooled.

Zinc

แปลว่า(english) Chemical Symbol Zn. Element No. 30 of the periodic system; atomic weight 65.38. Blue-white metal; when pure, malleable and ductile even at ordinary temperatures; melting point 787 (degrees) F.; boiling point 1665 (degrees) F., specific gravity 7.14. Can be electrodeposited; it is extensively used as a coating for steel and sheet zinc finds many outlets, such as dry batteries, etc. Zinc-base alloys are of great importance in die casting. Its most important alloy is brass.

Aging 2

แปลว่า(english) A change in properties that occurs at ambient or moderately elevated temperatures after hot working or a heat treating operation (quench aging in ferrous alloys), or after a cold working operation (strain aging). The change in properties is often, but not always, due to a phase change (precipitation), but does not involve a change in chemical composition. In a metal or alloy, a change in properties that generally occurs slowly at room temperature and more rapidly at higher temperatures.