Water Vapor Pressure

แปลว่า(Concrete Engineering) The pressure exerted by water vapor. Air that contains higher amounts of water vapor exerts a higher vapor pressure than air which has a lower amount of has a higher water vapor pressure In concrete water vapor pressure is calculated by the difference between the vapor pressure of the concrete and the ambient relative humidity and temperature and in contact with the soil. that is calculated by; based upon relative humidity and temperature. The greater the difference between the water vapor and ambient humidity and temperature, in degrees Fahrenheit. the greater the water vapor pressure exerted.

Flexibility:

แปลว่า(english) Flexibility is the inverse of stiffness. When a force is applied to a structure, there is a displacement in the direction of the force; flexibility is the ratio of the displacement divided by the force. High flexibility means that a small load produces a large displacement.

Aging 1

แปลว่า(english) A change in the properties of certain metal and alloys (such as steel) that occurs at ambient or moderately elevated temperatures after a hot working heat treatment or cold working operation. Typical properties impacted are hardness, yield strength, tensile strength, ductility, impact value, formability, magnetic properties, etc. See also Non-aging.

Blasting (Blast Cleaning)

แปลว่า(english) A process for cleaning or finishing metal objects by use of an air blast or centrifugal wheel that throws abrasive particles against the surface of the work pieces. Small, irregular particles of steel or iron are used as the abrasive in grit blasting, and steel or iron balls in shot blasting.

Normal strain:

แปลว่า(english) Strain measuring the intensity of deformation along an axis. Normal strain is usually denoted by . Average normal strain between two points is calculated as (Delta L / L), where L is the original distance between the points, and L is the change in that distance. Normal strain is often simply called strain.

Agglomerating Processes

แปลว่า(english) "Fine particles of limestone (flux) and iron ore are difficult to handle and transport because of dusting and decomposition, so the powdery material usually is processed into larger pieces. The raw material's properties determine the technique that is used by mills. 1) SINTER Baked particles that stick together in roughly one-inch chunks. Normally used for iron ore dust collected from the blast furnaces. 2) PELLETS Iron ore or limestone particles are rolled into little balls in a balling drum and hardened by heat. 3) BRIQUETTES Small lumps are formed by pressing material together. Hot Iron Briquetting (HBI) is a concentrated iron ore substitute for scrap for use in electric furnaces.

Water-Cement Ratio

แปลว่า(Concrete Engineering) The ratio of the amount of water, exclusive of that absorbed by the aggregates, to the amount of cement in a concrete mix. Typically expressed as percentage of water, by weight in pounds, to the total weight of portland cement, fly ash, and any other cementitious material, per cubic yard, exclusive of any aggregates.

Box Annealing

แปลว่า(english) Annealing a metal or alloy in a sealed container under conditions that minimize oxidation. In box annealing a ferrous alloy, the charge is usually heated slowly to a temperature below the transformation range, but sometimes above or within it, and is then cooled slowly; this process is also called close annealing or pot annealing.

Brass

แปลว่า(english) An alloy that is 70% copper,30% zinc. One of the most widely used of the copper-zinc alloys; malleable and ductile; excellent cold-working but poor hot-working and machining properties; excellent for soft-soldering; good for silver alloy brazing or oxyacetylene welding, but fair for resistance or carbon-arc welding. Used for drawn cartridges, tubes, eyelets machine items and snap fasteners.

Blast Furnace Slag

แปลว่า(Concrete Engineering) A non-metallic waste product developed in the manufacture of pig iron, consisting basically of a mixture of lime, silica and alumina, the same oxides that make up portland cement, but not in the same proportions or forms. It is used both in the manufacture of portland blast furnace slag cement and as an aggregate for lightweight concrete.

Billet 2

แปลว่า(english) A solid semi-finished round or square product that has been hot worked by forging, rolling, or extrusion. An iron or steel billet has a minimum width or thickness of 1 1/2 in. and the cross-sectional area varies from 2 1/4 to 36 sq. in. For nonferrous metals, it may also be a casting suitable for finished or semi-finished rolling or for extrusion.

Strength:

แปลว่า(english) A very general term that may be applied to a material or a structure. In a material, strength refers to a level of stress at which there is a significant change in the state of the material, e.g., yielding or rupture. In a structure, strength refers to a level of level of loading which produces a significant change in the state of the structure, e.g., inelastic deformations, buckling, or collapse.