Bevel

แปลว่า(english) Angle formed between the prepared edge of the end of tube and a plane perpendicular to the surface. Standard pipe bevel is 30 degrees.

Toxicity

แปลว่า(Environmental Engineering) A U.S. EPA hazardous waste characteristic defined with a rigorous test procedure, the TCLP (for Toxicity Characteristic Leaching Procedure). In the procedure, a waste is extracted for 24 hours with an acetic acid solution. The acid extract is then analyzed for the presence of any of the contaminants listed in the procedure.

Blast Furnace Slag

แปลว่า(Concrete Engineering) A non-metallic waste product developed in the manufacture of pig iron, consisting basically of a mixture of lime, silica and alumina, the same oxides that make up portland cement, but not in the same proportions or forms. It is used both in the manufacture of portland blast furnace slag cement and as an aggregate for lightweight concrete.

Retempering

แปลว่า(Concrete Engineering) The addition of water and remixing of concrete which has started to stiffen: usually not allowed as it may affect the ultimate strength.

Cement Content

แปลว่า(Concrete Engineering) A quantity of cement contained in a unit volume of concrete or mortar, ordinarily expressed as pounds, barrels, or bags per cubic yard.

Baseline

แปลว่า(Software Engineering) a point at which some deliverable produced during the software engineering process is put under formal change contro เส้นอ้างอิง ใช้สำหรับการวางผัง หรือการสำรวจ

Bainite

แปลว่า(english) A eutectoid transformation product of ferrite and a fine dispersion of carbide, generally formed at temperatures below 840 to 930 F (450 to 500 C): upper bainite is an aggregate containing parallel lath-shape units of ferrite, produces the so-called feathery appearance in optical microscopy, and is formed at temperatures above about 660 F (350 C); lower bainite consists of individual plate-shape units and is formed at temperatures below about 660 F (350 C). Also, a slender, needle-like (acicular) microstructure appearing in spring steel strip characterized by toughness and greater ductility than tempered Martensite. Bainite is a decomposition product of Austenite best developed at interrupted holding temperatures below those forming fine pearlite and above those giving Martensite.

Equilibrium:

แปลว่า(english) An object is in equilibrium if the resultant of the system of forces acting on it has zero magnitude. See static equilibrium and dynamic equilibrium.

Blast Furnace

แปลว่า(english) 1) A furnace in which solid fuel (limestone, coke, iron ore) is combined with high-pressure, hot air blast (120,000 psi) to smelt ore in a continuous process (They are never stopped. They can be slowed down or idled). A Blast Furnace in the iron and steel industry is used to produce liquid iron.

HRM High Reactivity Metakaolin

แปลว่า(Concrete Engineering) Refined form of an ASTM C618, Class N (natural) pozzolan. A high performance, mineral admixture, similar in performance to silica fume, additionally comparable in cost. Pure white powdered in form will, not effect the natural color or darken concrete as silica fume does. Suitable for high-performance color matching in architectural concrete. Dosage at 5% to 10%, of cement by weight. No bleed water, better finishability, more creamy, cleanup is easier with slightly higher 28 day strengths and 25% - 35% less plasticizer is required than silica fume.

Bandsaw

แปลว่า(english) A power saw, the blade of which is a continuous,narrow,steel band having teeth on one edge and passing over two large pulley wheels.

Acid Brittleness (Pickling Brittleness)

แปลว่า(english) Brittleness resulting from pickling steel in acid; hydrogen, formed by the interaction between iron and acid, is partially absorbed by the metal, causing acid brittleness.