Blue Brittleness

แปลว่า(english) Brittleness exhibited by some steels after being heated to some temperature within the range of 300 (degrees) to 650 (degrees) F, and more especially if the steel is worked at the elevated temperature. Killed steels are virtually free of this kind of brittleness.

Batch Anneal

แปลว่า(english) The process by which a large, stationary stack of steel coils (4 coils high) is subjected to a long heat-treating cycle. This process enables the cold-rolled sheet to fully recrystallize into the softest possible product conforming to customer specifications. Controlling the recrystallization process makes a fine-grained microstructure easy to obtain, and minimizes the tendencies for retention of directional properties of the rolled steel which could produce undesirable shapes in the stamping of a cylindrical part such as a can. Also see Anneal and Continuous Anneal.

Basic Oxygen Furnace (BOF)

แปลว่า(english) "WHAT A pear-shaped furnace, lined with refractory bricks, that refines molten iron from the blast furnace and scrap into steel. Up to 30% of the charge into the BOF can be scrap, with hot metal accounting for the rest. WHY BOFs, which can refine a heat (batch) of steel in less than 45 minutes, replaced open-hearth furnaces in the 1950s; the latter required five to six hours to process the metal. The BOF's rapid operation, lower cost and ease of control give it a distinct advantage over previous methods. HOW Scrap is dumped into the furnace vessel, followed by the hot metal from the blast furnace. A lance is lowered from above, through which blows a high-pressure stream of oxygen to cause chemical reactions that separate impurities as fumes or slag. Once refined, the liquid steel and slag are poured into separate containers. "

Base Box

แปลว่า(english) Unit of area of 112 sheets of tin mil products (tin plate, tin free steel or black plate) 14 by 20 inches, or 31,360 square inches. Tin Plate is sold, and carried in finished inventory, on a weight per unit area rather than on a thickness basis.

Aging 1

แปลว่า(english) A change in the properties of certain metal and alloys (such as steel) that occurs at ambient or moderately elevated temperatures after a hot working heat treatment or cold working operation. Typical properties impacted are hardness, yield strength, tensile strength, ductility, impact value, formability, magnetic properties, etc. See also Non-aging.

Blast Furnace

แปลว่า(english) 1) A furnace in which solid fuel (limestone, coke, iron ore) is combined with high-pressure, hot air blast (120,000 psi) to smelt ore in a continuous process (They are never stopped. They can be slowed down or idled). A Blast Furnace in the iron and steel industry is used to produce liquid iron.

Brinell Hardness Test

แปลว่า(english) A common standard method of measuring the hardness of materials. The smooth surface of the metal is subjected to indentation by a hardened steel ball under pressure. The diameter of the indentation, in the material surface, is then measured by a microscope and the hardness value is read from a chart or determined by a prescribed formula.

Billet 2

แปลว่า(english) A solid semi-finished round or square product that has been hot worked by forging, rolling, or extrusion. An iron or steel billet has a minimum width or thickness of 1 1/2 in. and the cross-sectional area varies from 2 1/4 to 36 sq. in. For nonferrous metals, it may also be a casting suitable for finished or semi-finished rolling or for extrusion.

Boron (chemical symbol B)

แปลว่า(english) Element N. 5 of the periodic system. Atomic weight 10.82. It is gray in color, ignites at about 1112 (degrees) F. and burns with a brilliant green flame, but its melting point in a non-oxidizing atmosphere is about 4000 (degrees) F. Boron is used in steel in minute quantities for one purpose only- to increase the hardenability as in case hardening and to increase strength and hardness penetration.

Age Hardening

แปลว่า(english) Hardening by aging, usually after rapid cooling or cold working. The term as applied to soft, or low carbon steels, relates to a wide variety of commercially important, slow, gradual changes that take place in properties of steels after the final treatment. These changes, which bring about a condition of increased hardness, elastic limit, and tensile strength with a consequent loss in ductility, occur during the period in which the steel is at normal temperatures.

Zinc

แปลว่า(english) Chemical Symbol Zn. Element No. 30 of the periodic system; atomic weight 65.38. Blue-white metal; when pure, malleable and ductile even at ordinary temperatures; melting point 787 (degrees) F.; boiling point 1665 (degrees) F., specific gravity 7.14. Can be electrodeposited; it is extensively used as a coating for steel and sheet zinc finds many outlets, such as dry batteries, etc. Zinc-base alloys are of great importance in die casting. Its most important alloy is brass.

Bainite

แปลว่า(english) A eutectoid transformation product of ferrite and a fine dispersion of carbide, generally formed at temperatures below 840 to 930 F (450 to 500 C): upper bainite is an aggregate containing parallel lath-shape units of ferrite, produces the so-called feathery appearance in optical microscopy, and is formed at temperatures above about 660 F (350 C); lower bainite consists of individual plate-shape units and is formed at temperatures below about 660 F (350 C). Also, a slender, needle-like (acicular) microstructure appearing in spring steel strip characterized by toughness and greater ductility than tempered Martensite. Bainite is a decomposition product of Austenite best developed at interrupted holding temperatures below those forming fine pearlite and above those giving Martensite.