Billet 2

แปลว่า(english) A solid semi-finished round or square product that has been hot worked by forging, rolling, or extrusion. An iron or steel billet has a minimum width or thickness of 1 1/2 in. and the cross-sectional area varies from 2 1/4 to 36 sq. in. For nonferrous metals, it may also be a casting suitable for finished or semi-finished rolling or for extrusion.

Vibration

แปลว่า(Concrete Engineering) Energetic agitation of concrete to assist in its consolidation, produced by mechanical oscillating devices at moderately high frequencies. (A.) External vibration employs a device attached to the forms and is particularly applicable to the manufacture of precast items and for the vibration of tunnel lining forms. (B.) Internal vibration employs an element which can be inserted into the concrete; and is more generally used for cast-in-place construction.

Absolute Volume

แปลว่า(Concrete Engineering) The volume of an ingredient in its solid state, without voids between individual pieces or particles, in the case of fluids, the cubic content occupied. In concrete, the actual volume occupied by the different ingredients determined by dividing the weight of each ingredient pounds, by ifs specific gravity, times the weight of one cubic foot of water in pounds. Example: Absolute Volume of one sack of cement equals: 94 ๗ (3.15X62.4) = 0.478 cubic feet

Brazing

แปลว่า(english) Joining metals by fusion of nonferrous alloys that have melting points above 800 F (425C), but lower than those of the metals being joined. May be accomplished by a torch. Filler metal is ordinarily in rod form in torch brazing; whereas in furnace and dip brazing the work material is first assembled and the filler metal may then be applied as wire, washers, clips, bands, or may be bonded, as in brazing sheet.

HRM High Reactivity Metakaolin

แปลว่า(Concrete Engineering) Refined form of an ASTM C618, Class N (natural) pozzolan. A high performance, mineral admixture, similar in performance to silica fume, additionally comparable in cost. Pure white powdered in form will, not effect the natural color or darken concrete as silica fume does. Suitable for high-performance color matching in architectural concrete. Dosage at 5% to 10%, of cement by weight. No bleed water, better finishability, more creamy, cleanup is easier with slightly higher 28 day strengths and 25% - 35% less plasticizer is required than silica fume.

Bend Test

แปลว่า(english) Various tests which is used to ascertain the toughness and ductility of a metal product, in which the material is bent around its axis and/ or around an outside radius. A complete test might specify such a bend to be both with and against the direction of grain. For testing, samples should be edge filed to remove burrs and any edgewise cracks resulting from slitting or shearing. If a vice is to be employed, then you must line the jaws with some soft metal, to permit a flow of the metal in the piece being tested.

Black Oil Tempered Spring Steel Strip (Scaleless Blue)

แปลว่า(english) A flat cold rolled usually .70/.80 medium high carbon steel strip, blue-black in color, which has been quenched in oil and drawn to desired hardness. While it looks and acts much like blue tempered spring steel and carries a Rockwell hardness of C44/47, it has not been polished and is lower in carbon content. Used for less exacting requirements than clock spring steel, such as snaps, lock springs, hold down springs, trap springs, etc. It will take a more severe bend before fracture than will clock spring, but it does not have the same degree of spring-back.

Bainite

แปลว่า(english) A eutectoid transformation product of ferrite and a fine dispersion of carbide, generally formed at temperatures below 840 to 930 F (450 to 500 C): upper bainite is an aggregate containing parallel lath-shape units of ferrite, produces the so-called feathery appearance in optical microscopy, and is formed at temperatures above about 660 F (350 C); lower bainite consists of individual plate-shape units and is formed at temperatures below about 660 F (350 C). Also, a slender, needle-like (acicular) microstructure appearing in spring steel strip characterized by toughness and greater ductility than tempered Martensite. Bainite is a decomposition product of Austenite best developed at interrupted holding temperatures below those forming fine pearlite and above those giving Martensite.

Brown Sharp Gages

แปลว่า(english) A standard series of sizes refered to by numbers, in which the diameter of wire or thickness of sheet metal is generally produced and which is used in the manufacture of brass, bronze, copper, copper-base alloys and aluminum. These gage numbers have a definite relationship to each other. In this system, the decimal thickness is reduced by 50% every six gage numbers- while temper is expressed by the number of B&S gage numbers as cold reduced in thickness from previous annealing. For each B&S gage number in thickness reduction, where is assigned a hardness value of 1/4 hard.

Carbonation

แปลว่า(Concrete Engineering) 1) Reaction between the products of portland cement (soluble calcium hydroxides), water and carbon dioxide to produce insoluble calcium carbonate (efflorescence). 2) Soft white, chalky surface dusting of freshly placed, unhardened concrete caused by carbon dioxide from unvented heaters or gasoline powered equipment in an enclosed space. 3) Carbonated, dense, impermeable to absorption, top layer of the surface of concrete caused by surface reaction to carbon dioxide. This carbonated layer becomes denser and deeper over a period of time. 4) Reaction with carbon dioxide which produces a slight shrinkage in concrete. Improves chemical stability. Concrete masonry units during manufacturing may be deliberately exposed to carbon dioxide after reaching 80% strength to induce carbonation shrinkage to make the units more dimensionally stable. Future drying shrinkage is reduced by as much as 30%.

Bent Axis Pumps

แปลว่า(english) In this pump, the pistons are at an angle to the drive shaft and Thrust Plate. The piston block shaft is connected to the drive shaft by a universal joint, not shown. The drive shaft, thrust plate, piston block shaft, and piston block all revolve. The connecting rods are attached to the thrust plate and revolve with it, unlike the swash plate pump where the piston rods slide past a stationary swash plate. The outlet ports are semi-circular holes in the Valve Plate, shown on the far right of the animation on edge and in a head-on view below, right. As the pump revolves, half the pistons suck in fluid as they pass over the intake port. The other pistons discharge their fluid through the outlet port. This pump should be compared to the radial piston pump, swash plate pump, and wobble pump.