Z-Mill

แปลว่า(english) The full name for z-mill is Sendzimir mill. A Z-mill operates with a very small diameter work roll, normally about 2 inches, backed up by a number of rolls in a pyramid-shaped stack. This roll set up allows you to exert extremely high forces through the work roll and yet keep the work roll from extreme flexing. The take-up roll on the Z-Mill also exerts a tension on the coil as it comes through the mill. The combination of high pressure and tension makes the mill capable of rolling material thin and flat.

Couple:

แปลว่า(english) A system of forces composed of two equal forces of opposite direction, offset by a distance. A couple is statically equivalent to a moment whose magnitude equals the magnitude of the force times the offset distance.

Autotrophic

แปลว่า(Environmental Engineering) Organisms which utilize inorganic carbon for synthesis of protoplasm. Ecologists narrow the definition further by requiring that autotrophs obtain their energy from the sun. In microbiologist parlance, this would be a photoautotroph. See photoautotrophic and chemoautotrophic.

Cement, Portland (ASTM C150) (Concrete Engineering)

แปลว่าA powdery substance made by burning, at a high temperature, a mixture of clay and limestone producing lumps called “clinkers” which are ground into a fine powder consisting of hydraulic calcium silicates. For non-portland cements, see aluminous cement.

Peeling

แปลว่า(Concrete Engineering) A process in which thin flakes of matrix or mortar are broken away from concrete surface; caused by adherence of surface mortar-to forms as forms are removed, or to trowel or float in portland cement plaster.

Statically determinate:

แปลว่า(english) A statically determinate structure is one where there is only one distribution of internal forces and reactions which satisfies equilibrium. In a statically determinate structure, internal forces and reactions can be determined by considering nothing more than equations of equilibrium.

Bearing Strength

แปลว่า(english) The maximum bearing load at failure divided by the effective bearing area. In a pinned or riveted joint, the iffective area is calculated as the product of the diameter of the hole and the thickness of the bearing member.

Carbonation

แปลว่า(Concrete Engineering) 1) Reaction between the products of portland cement (soluble calcium hydroxides), water and carbon dioxide to produce insoluble calcium carbonate (efflorescence). 2) Soft white, chalky surface dusting of freshly placed, unhardened concrete caused by carbon dioxide from unvented heaters or gasoline powered equipment in an enclosed space. 3) Carbonated, dense, impermeable to absorption, top layer of the surface of concrete caused by surface reaction to carbon dioxide. This carbonated layer becomes denser and deeper over a period of time. 4) Reaction with carbon dioxide which produces a slight shrinkage in concrete. Improves chemical stability. Concrete masonry units during manufacturing may be deliberately exposed to carbon dioxide after reaching 80% strength to induce carbonation shrinkage to make the units more dimensionally stable. Future drying shrinkage is reduced by as much as 30%.

GFRC - Glass Fiber Reinforced Concrete

แปลว่า(Concrete Engineering) Concrete panels, usually architectural designs, reinforced with a high zirconia (16% minimum), alkali-resistant glass fiber. Optimum glass fiber content of 5% by weight. Lower fiber content results in lower early ultimate strengths, higher fiber content can produce composite compaction and consolidation difficulties.

Cell

แปลว่า(Environmental Engineering) A unit of varying dimensions in a landfill which is isolated from the environment by 6 to 12 inches of soil cover. A cell is one day's waste or less. A cell is covered with soil at the end of each day.

Unit Water Content

แปลว่า(Concrete Engineering) The quantity of water per unit volume of freshly mixed concrete, often expressed as gallons or pounds per cubic yard. This is the quantity of water on which the water cement ratio is based, and does not include water absorbed by the aggregate

Blue Brittleness

แปลว่า(english) Brittleness exhibited by some steels after being heated to some temperature within the range of 300 (degrees) to 650 (degrees) F, and more especially if the steel is worked at the elevated temperature. Killed steels are virtually free of this kind of brittleness.