Blush

แปลว่า(english) A coating defect consisting of the whitening of a cured film which results in a translucent or opaque appearance with accompanying loss of gloss. Blushing usually occurs during the pasteurization or steam processing of films which are undercured or water sensitive.

Blow

แปลว่า(english) The impact or force delivered by one workstroke of the forging equipment.

Mixing Speed

แปลว่า(Concrete Engineering) Rate of mixer drum rotation or that of the paddles in a pan, open-top, or trough type mixer, when mixing a batch; expressed in revolutions per minute (rpm) or in peripheral] feet per minute of A point on the circumference at maximum diameter.

Sulfate Attack

แปลว่า(Concrete Engineering) Deleterious chemical and/or physical re-action between sulfates in ground water or soil and certain constituents in cement, which result in expansion and disruption of the concrete.

Risk

แปลว่า(Software Engineering) a potential problem or occurrence that put a project in jeopardy ความเสี่ยง

Stepwise refinement

แปลว่า(Software Engineering) a technique for accomplishing functional decomposition or procedural design (also called partitioning)

Ductility:

แปลว่า(english) Ductility generally refers to the amount of inelastic deformation which a material or structure experiences before complete failure. Quantitatively, ductility can be defined as the ratio of the total displacement or strain at failure, divided by the displacement or strain at the elastic limit.

Blister 2

แปลว่า(english) A defect in metal, on or near the surface, resulting from the expansion of gas in a subsurface zone. Very small blisters are called pinheads or pepper blisters.

Sulfate Resistance

แปลว่า(Concrete Engineering) Ability of cement paste, aggregate, or mixtures thereof to withstand sulfate attack.

Nitrogen fixation

แปลว่า(Environmental Engineering) The conversion of atmospheric (or dissolved) nitrogen gas into nitrate by microorganisms.

Breakout

แปลว่า(english) An accident caused by the failure of the walls of the hearth of the furnace resulting in liquid iron or slag (or both) flowing uncontrolled out of the blast furnace.

Burn

แปลว่า(english) 1) Process of cutting metal by a stream of fuel and oxygen, 2) to permanently damage a metal or alloy by heating to cause either incipient melting or intergranular oxidation.